【摘 要】
：
P_2O_5-V_2O_5-TiO_2(简写为P-V-Ti)对芳烃氧化有良好的催化效果.丁烷氧化催化剂P-V体系的体相和表面结构已有一些报道.但P_2O_5对V-Ti的影响文献较少报道.本文用XRD,IR,TPD
【机 构】
：
哈尔滨师范大学表面化学研究所,哈尔滨师范大学表面化学研究所,哈尔滨师范大学表面化学研究所
论文部分内容阅读
P_2O_5-V_2O_5-TiO_2(简写为P-V-Ti)对芳烃氧化有良好的催化效果.丁烷氧化催化剂P-V体系的体相和表面结构已有一些报道.但P_2O_5对V-Ti的影响文献较少报道.本文用XRD,IR,TPD和ESR考察了P-V-Ti体系. 1.试剂和催化剂:草酸、偏钒酸铵、二氧化钛均为化学纯.将V_2O_5:TiO_2=11:89(重量)样品分别按 P/V原子比为0.1,0.3,0.6,1.0,1.5和2.5制成编号为P-0.1,P-0.3,P-O.6,P-1.0,P-1.5和P-2.5的催化剂.
P_2O_5-V_2O_5-TiO_2 (abbreviated as PV-Ti) has a good catalytic effect on the oxidation of aromatics.But the phase structure and surface structure of butane oxidation catalyst PV system have been reported, but the impact of P_2O_5 on V-Ti is less reported The PV-Ti system was investigated by XRD, IR, TPD and ESR. 1. Reagents and catalysts: oxalic acid, ammonium metavanadate and titanium dioxide were all chemically pure. Samples of V 2 O 5: TiO 2 = 11: 89 The P / V atomic ratios of 0.1, 0.3, 0.6, 1.0, 1.5 and 2.5 were made as catalysts numbered P-0.1, P-0.3, PO.6, P-1.0, P-1.5 and P-2.5.
其他文献
采用有色金属合金作为模具材料具有制模简单、周期短、制件表面不易被划伤等优点。目前在国内外已有很大发展。一九七三年研制成功58％Bi(铋)、42％Sn(锡)的合金模具,并于一九七
鲇鱼系底栖肉食性鱼类,多生活在较深水域底层。常在坡底、陡坎、树桩、石缝、洞穴处聚居。鲇喜有水流的地方,常隐匿在这些地方等待食物。当其一旦发现猎物便迅猛出击,咬住后
目的:探讨特发性血小板减少性紫癜(ITP)患者血清中血小板生成调控因子血小板生成素(TPO)和转化生长因子β1(TGF-β1)的变化并探讨其临床意义。方法:采用双抗体夹心ELISA检测3
前言近年来,由于我国少无切削的冷镦、冷挤压先进工艺迅速发展,要求钢材表面具有良好的润滑层,而磷化皂化薄膜是目前世界上普遍用于冷塑变形的润滑膜。当前国内外磷化溶液的
文章结合《仿生工程学报》编辑部工作实际,探讨Scopus在发掘潜在读者、作者进行文章推送,查找和评估邀稿对象,研究热点分析以及期刊自我评估等方面的应用。这些实际应用表明,
在0.05—0.8MH_3PO_4介质,Ta(Ⅴ)与H_2O_2形成H_2O_2—Ta—H_3PO_4三元络合物,络合物中Ta∶H_2O_2=1∶1。借助定量加入过量的H_2O_2使与Ta结合,然后用KMnO_4滴定剩余的H_2O_2
青海山川机床铸造厂重型车间的大炉送料采用HMT524卷扬机系统,这种爬式加料机的设计存在一些问题,由于滚筒太短,而钢丝绳长,造成上料时夹角太小,与两滑轮的夹角更小,钢丝绳
在混气电解加工中,气液混合比是决定其工艺现象的主导因素。摸索与总结气液混合比与工艺现象之间的规律是进一步发挥混气电解加工效果必需解决的问题。而其中一个主要的而带
用~(60)Coγ源辐照TBP体系,研究了TBP与溶质分子反式二苯乙烯、TOA、TEA、吡啶的能量转移机理。实验发现,在能量接受体(反式二苯乙烯,三烷基胺)的电离电位低于TBP的电离电位
Ⅰ 引言 光电子转移(ET)反应分解水受到广泛重视,虽然要实现大规模太阳能储存还有很多问题待解决;但近年进展很大。在光解硫化氢、光还原二氧化碳、光助电解水等方面也有进