【摘 要】
：
Titanium (Ti) nitrides were in situ grown on Ti6Al4V alloy (TA) using a glow discharge plasma nitriding (GDPN). The morphology, chemical composition, phase and mechanical property of the obtained nitrided TA were analyzed using a scanning electron microsc
【机 构】
：
College of Mechanical Engineering,Donghua University,Shanghai 201620,China
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Titanium (Ti) nitrides were in situ grown on Ti6Al4V alloy (TA) using a glow discharge plasma nitriding (GDPN). The morphology, chemical composition, phase and mechanical property of the obtained nitrided TA were analyzed using a scanning electron microscope (SEM), energy dispersive spectroscope (EDS), X-ray diffraction (XRD), and nanoindentation tester, respectively. The tribological performances of un-nitrided and nitrided TAs were evaluated using a ball-on-plate wear tester, and the wear mechanism was also discussed in detail. The results show that the nitrided layer with the compound and diffusion layers is formed on the nitrided TA, which is composed of δ-TiN and a-Ti phases. The nanohardness and elastic modulus of nitrided TA are 6.05 and 143.13 GPa, respectively, higher than those of un-nitrided TA. The friction reduction and anti-wear performances of nitrided TA are better than those of un-nitrided TA, and the wear mechanism is primary abrasive wear, accompanying with adhesive wear, which is attributed to the formation of Ti nitrides with the high nanohardness and elastic modulus.
其他文献
The waste coffee-grounds carbon (WCGC) was prepared with H3PO4 treated using waste coffee-grounds as precursor. Its adsorption ability was studied using phenol as test molecule. The influence of H3PO4 treated, calcined temperature, the initial phenol conc
To solve the problem of the poor plasticity and to meet the requirements of high temperature for forming titanium alloy, mechanical properties of TC2 titanium alloy under the compound energy-field (CEF) with temperature and ultrasonic vibration were studi
Graphene-modified asphalt (GMA) for road application was prepared via using metal-free phthalocyanine-dispersed to modify an SK-70# base asphalt with graphene. The preparation parameters are as follows: the content of graphene is 0.26％ based on the mass p
To investigate the dynamic recrystallization behavior of 7xxx aluminum alloys, the isothermal compression tests were carried on the 7056 aluminum alloy in the temperatures range of 320-440 ℃ and in the strain rates range of 0.001-1 s-1. In addition, the m
The influence of rare earth Y on the microstructure and mechanical properties of Al-Zr alloy produced by dynamic ECAE was studied by OLYMPUS-BX51M optical microscope (OM), S4800 energy disperse spectroscopy (EDS) and SANS CMT5105 electronic universal mate
An efficient and promising approach for effectively dispersing multi-walled carbon nanotubes (MWCNTs) in cementitious composites has been investigated. The naturally occurring organic extracts from species of indigenously known \'Keekar\' trees scatte
The microstructure evolution and its effects on the mechanical performance of 2000 MPa bridge cable steel wires were investigated by transmission electron microscope (TEM), electron backscatter diffraction (EBSD), X-ray diffractometer (XRD) and mechanical
The 2024 anodized aluminum alloy film was sealed by KAl(SO4)2 solution and the effect of sealing on corrosion resistance was investigated by means of potentiodynamic polarization curves, electrochemical impedance spectroscopy, and X-ray photoelectron spec
Fe-Al-Ta eutectic composites with solidification rates of 6, 20, 30, 80 and 200μm/s were obtained by a modified Bridgman directional solidification technique and alloying. Moreover, tensile property and fracture behavior of Fe-Al-Ta eutectic composites we
全球工业化水平的持续提升加速了煤、石油、天然气等化石燃料的消耗, 大量二氧化碳(CO2)被排放进大气, 导致全球变暖和生态失衡, 削减 CO2 排放、将CO2资源化成为亟需解决的问题.2010年前后, 美国、欧洲、日本相继开启以“人工光合成”为题的国家级科研项目, 投入经费均在1亿美元以上.2011年起, 我国国家自然科学基金委、科技部相继资助了相关项目.2020年9月, 我国政府进一步提出力争在2030年前实现“碳达峰”、2060年前实现“碳中和”的目标.