由烟台师范学院应用化学研究所研制的SN-1型镀镍光亮剂、新型宽温度氯化钾(钠)镀锌光亮剂于1992年8月26日通过了由山东省科委组织的技术成果鉴定.来自省内的专家们认为,SN-1型镀镍光亮剂与国外同类产品相比,其沉积速度快、光亮范围宽、镀层韧性好,且价格适中,易被电镀厂家所接受;新型宽温度氯化钾(钠)镀锌光亮剂可在5～70℃的镀液中镀出质量良好的镀层,且乳化性能强,优于目前国内使用的宽温度载体.鉴定委员会一致认为,该研究填补了省内空白,建议尽快组织批量生产.
The SN-1 nickel plating brightener developed by the Institute of Applied Chemistry, Yantai Teachers College, the new wide temperature potassium chloride (sodium) zinc brightener passed the technological achievements organized by Shandong Science and Technology Commission on August 26, Experts from the province believe that SN-1-type nickel brightener compared with similar foreign products, the deposition speed, wide range of bright, good coating toughness, and affordable, easy to be accepted by the electroplating factory; new Wide temperature potassium chloride (sodium) zinc plating brightener plating bath at 5 ~ 70 ℃ good quality coating, and the emulsification performance is better than the current wide temperature carrier used in China. Accreditation Committee agreed that the Research to fill gaps in the province, it is recommended to organize mass production as soon as possible.