1项目研究背景1.1 Solidia Cement~(TM)与波特兰水泥熟料生产过程的区别Solidia Cement~(TM)硅酸钙基胶凝材料的生产工艺,与传统波特兰水泥熟料基本相同,一是所使用原材料基本相同,二是生产烧成过程相同;不过它与波特兰水泥熟料相比,也存在多个鲜明的特征。▲烧成回转窑内的煅烧温度相对较低,仅约1200℃,比波特兰水泥熟料烧成温度低约150℃。▲Solidia Cement~(TM)烧成过程中的CO_2排放量,约
1 Project Background 1.1 The difference between the production process of Solidia Cement TM and Portland cement clinker Solidia Cement TM calcium silicate based cementitious material has the same production process as the traditional Portland cement clinker, First, the same basic raw materials used, and second, the same process of production and firing; but it has many distinctive features compared with Portland cement clinker. ▲ calcination rotary kiln firing temperature is relatively low, only about 1200 ℃, lower than Portland cement clinker burning temperature of about 150 ℃. ▲ Solidia Cement ~ (TM) CO 2 emissions during firing, approx