【摘 要】
：
ＢＮｂＲＥ（包钢铌稀土）重轨属９８０ＭＰａ级高强度耐磨钢轨，它比Ｕ７４提高耐磨性能１．２倍，提高接触疲劳性能１．１倍，且具有良好的综合性能。稀土能明显改变夹杂物形态，Ｎｂ、ＲＥ能有效地提高钢轨的表面硬度，细化晶粒，减小珠光体
论文部分内容阅读
ＢＮｂＲＥ（包钢铌稀土）重轨属９８０ＭＰａ级高强度耐磨钢轨，它比Ｕ７４提高耐磨性能１．２倍，提高接触疲劳性能１．１倍，且具有良好的综合性能。稀土能明显改变夹杂物形态，Ｎｂ、ＲＥ能有效地提高钢轨的表面硬度，细化晶粒，减小珠光体片间距
BNbRE (Baotou Steel niobium rare earth) heavy rail is 980MPa high-strength wear-resistant rail, which improves the wear resistance than U74 1.2 times, improve contact fatigue performance 1.1 times, and has good overall performance. Rare earth can significantly change the morphology of inclusions, Nb, RE can effectively improve the surface hardness of the rail, grain refinement, reducing pearlite sheet spacing
其他文献
Single-phase and gas-liquid two-phase pressure drops caused by a sudden con-traction in microtubes were experimentally investigated at room temperature and atmo
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
阜阳市局 ￡4a 局长——_MINtkMMtgj’＃lnH＄B——q.M——D收束志不他只邀狲位J则【科校为先导推动地租工作.B为广为戳民U用凶盼引眯B.习.互们羹宽.互狈槽竺汹IAn.刊 办好杂志。必
在裂纹技术理论和实践的基础上，从实验的角度，分析了应力法剪切的切口参数和长径比对剪切断面质量的影响规律．从宏观和细观两个方面探讨了周边切口的导向作用．
Based on the the
在1995年召开的全国科学大会上,党中央适时地重申并号召:要在全国坚定不移地实施科教兴国战略。科教兴国战略是指全面落实科学技术是第一生产力的思想,坚持教育为本,把科技
过二硫酸四丁铵使硫化物选择性氧化成亚砜ＣｈｅｎＦ等［ＳｙｎＣｏｍｍｕｎ，１９９６；２６：２５３］二烷基、二芳基或烷基芳基硫醚在二氯甲烷中与过二硫酸四丁铵［室温反应１～２ｈ得相应的亚砜，１１例收率９７．５５～９９．５％。未发现有副产物砜［杭轶萍摘俞雄校...
T
本刊讯(记者韩阳)5月17日,中国少年儿童新闻出版总社的“中少世博阅读,点亮智慧童年”全国校园行第一站北京启动,作为活动的第一站中少社携手“春蕾计划”走进了北大附小的孩
本文通过电化学方法探讨了Ｎａ_２ＷＯ_４·２Ｈ_２Ｏ对化学镀镍液的影响。局部阳极和局部阴极极化曲线说明，Ｎａ_２ＷＯ_４·２Ｈ_２Ｏ的加入对Ｈ_２ＰＯ_２~－的氧化反应和Ｎｉ~（２＋）的还原反应都有促进作用，这与实际中获得的Ｎａ_２ＷＯ_４·２Ｈ_２Ｏ对化学镀Ｎｉ－Ｗ－Ｐ
苄基四氢巴马汀对表达于非洲爪蟾卵母细胞及中华大蟾蜍卵母细胞的延迟整流钾电流的抑制作用童秋生，夏国瑾，姚伟星，江明性，白小川，包永德（同济医科大学基础医学院药理学教研室，武汉４３００３０；中
本文采用尿囊素在ｐＨ＝９．０的硼酸氯化钾缓冲液中由酮式转变成烯醇式结构，用不同的溶媒制成相同浓度的溶液，其差示光谱在２２５．５ｎｍ处有最大吸收，消除了杂质的干扰，平均回收率为９９．９５％，相对标准偏差为０．１８％。本法