【摘 要】
：
Ce-Zr compounds such as Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl f
【机 构】
：
Key Laboratory for Green Chemical Technology of State Education Ministry
【基金项目】
：
国家重点基础研究发展计划(973计划)
论文部分内容阅读
Ce-Zr compounds such as Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures and adhesion performance between the substrates and the washcoats were measured by SEM, BET surface area, ultrasonic vibration and thermal shock test. The results show that the addition of Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 into the slurries can improve γ-Al2O3-based washcoat adhesion on FeCrAl foils. Furthermore, ceria-zirconia solid solution increases the adhesion of the washcoat on the surface of an FeCrAl foil than the two others. The specific surface area of this washcoat remains about 43-45 m2/g and the weight loss is below 4.0% even after aging test of 10%steam-containing air at 1050℃ for 20 h.
其他文献
We report ab initio UMP2 calculations of the reaction of CN with HNCO using 6-311G(d,p) basis sets.The obtained results show that the reaction has two product c
In order to obtain the optimal parameters of anchor bolt supporting system for large-span and jointed rock mass in Kaiyang Phosphor Mine, it is expensive and un
The SrTiO3 (001) substrates treated by chemical etching in NH4F-buffered HF solution and annealing in oxygen ambient have been studied by an atomic force micros
Firstly, the cross large deflection equation of circular thin plate with variable thickness in rectangular coordinates system was transformed into unsymmetrical
Reliable turbulent channel flow databases at several Reynolds numbers have been established by large eddy simulation (LES), with two of them validated by compar
A multisensor image fusion algorithm is described using 2-dimensional nonseparable wavelet frame (NWF) transform. The source multisensor images are first decomp
主要对一般情形、含无风险资产和含外生负债三种情况下的TSF模型用直观解法求解,并对其最优解、可行解的存在性条件进行详细讨论,另外还提出一些值得进一步研究的问题.
With the help of an electromagnetic stirring device, alloy melt quenching and EBSD (electron back scatter diffraction)analysis technology, the microstructure of
The austenite medium Mn steel modified with controlled additions of Ca, Y, Si were directionally solidified using the vertical Bridgman method to study the effe
SrBi2.2Ta2O9(SBT) thin film with thickness of 2 μm was successfully prepared by sol-gel method, using strontium acetate semihydrate [Sr(CH3COO)2·1/2H2O] and b