【摘 要】
：
Co-intensification was researched to accelerate gold leaching with regards to its electrochemical nature by using anodic intensifiers of heavy metal ions (Pb2+,
【机 构】
：
School of Mineral Processing and Bioengineering
论文部分内容阅读
Co-intensification was researched to accelerate gold leaching with regards to its electrochemical nature by using anodic intensifiers of heavy metal ions (Pb2+, Bi3+, Tl+, Hg2+ and Ag+) on the basis of hydrogen peroxide assistant leaching on three different types of materials which were classified as a refractory sulphide gold concentrate, an easily leachable sulphide gold concentrate, and a low grade oxide gold ore according to their leaching characteristics. The results showed that, favorable co-intensification effects on the three materials were obtained and leaching time of gold was effectively shortened to no longer than 12 h from 16 to 24 h for hydrogen peroxide assistant leaching. For the five tested heavy metal ions, Bi3+and Tl+ presented co-intensifying effect on all the three materials, and Hg2+ caused co-intensifying effect on both refractory and easily leachable sulphide gold concentrates, and Pb2+ and Ag+ only had co-intensifying effect on the easily leachable sulphide gold concentrate.
其他文献
Methods of the comprehensive evaluation have been studied for many years.However,the change speed of evaluated objects was rarely considered by the existing eva
Vacuum distillation is a technique suitable for low boiling and melting point materials,to remove the heavy and low vapor pressure impurities at low level.As in
Large amount of high concentration acidic wastewater would be produced in the conversion process of chloride rare earth into oxide rare earth.It was a mixed sol
The accumulation of rare earth elements(REEs)in soil has occurred due to the pollution caused by the exploitation of rare earth resources and the wide rare eart
Two acid mine drainage (AMD) samples TS and WK, which were from the Dachang metals-rich mine in Guangxi province, China, were studied using PCR-based cloning ap
Cellular lightweight concrete (CLC) with the controlled density of approximately 800kg/m3 was made from a preformed foam, Type-I Portland cement (OPC), fly ash
Nickel and sulfate co-modified CeO2-ZrO2 catalysts were prepared by sol-gel method.The catalysts were characterized by XRD,FTIR,XPS,NH3 chemisorption and NH3-SC