【摘 要】
：
The delamination of kaolinite was performed via the combination of intercalation and sonication.The morphology including shape,size,and crystal structure before
【机 构】
：
School of Materials Science and Engineering,Institute of Hydrogen Technology
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The delamination of kaolinite was performed via the combination of intercalation and sonication.The morphology including shape,size,and crystal structure before and after the treatment were investigated by using XRD,SEM,TEM and SED(selective electron diffraction).The results not only show that the particle size is significantly reduced after short time sonication treatment,such as BET area up to 52.29m2/g after only 1 h sonication treatment,but also indicate that the treated particles keep good crystal structure.A new aluminum silicate nanoclub-like crystal formed after sonication treatment.
其他文献
We present an algorithm which can realize 3D stereo vision simultaneous localization and mapping (SLAM) for mobile robot in unknown outdoor environments, which
The cube texture and the surface corrosion structure of aluminum anode foil for high voltage electrolytic capacitor containing trace Sn were investigated based
The high water-cement ratio concrete specimens under biaxial compression that completed in a triaxial testing machine were experimentally studied.Strength and d
Boehmite nanorods were synthesized by a solvothermal method using AlCl3-6H2O in mixed solvents of water and aniline. The solvothermal time, heating temperature
The effect of rare earths (RE) surface treatment of carbon fibers (CF) on tribological properties of CF reinforced polytetrafluoroethylene (PTFE) composites und
The novel epoxidized soybean oil-modified-phenolic resin/clay nanocomposites(ESO-M-PR/CN)was prepared.The coupling agent-benzyldimethylphenylammonium chloride [
Tin was found in the bottom of float borosilicate glasses.To simulate the enriched amounts of SnO found on the surface of the float borosilicate glasses,a serie
Leucite particles were synthesized from feldspar mixed with 0%to 52%potassium nitrate fired from 800℃to 1200℃by solid state method.The X-ray Diffraction(XRD)p
岗位再设计是通过调整员工与工作有关的需求来提高工作效率的一种管理方法,而清溪沟学校虽然不是企业组织,追求教育教学质量一流与追求经济效益最大化的目标有天壤之别,但是
A two-step reheating process was proposed and applied to perform reheating experiments on the semi-solid 2024 alloy billet. In this process, the semi-solid bill