【摘 要】
：
采用电阻炉熔炼了Al-7.2Zn-2.2Mg-1.8Cu-0.2Zr和Al-7.2Zn-2.2Mg-1.8Cu-0.2Sc-0.2Zr两种铝合金,在700~720℃挤压铸造成形,并经过465℃×24h+475℃×8h水淬+120℃×24h时效热处
【机 构】
：
北京有色金属研究总院国家有色金属复合材料工程技术研究中心,
论文部分内容阅读
采用电阻炉熔炼了Al-7.2Zn-2.2Mg-1.8Cu-0.2Zr和Al-7.2Zn-2.2Mg-1.8Cu-0.2Sc-0.2Zr两种铝合金,在700~720℃挤压铸造成形,并经过465℃×24h+475℃×8h水淬+120℃×24h时效热处理。结果表明,Sc、Zr的复合添加能明显细化α-Al基体和晶间第二相;通过多级固溶和时效处理,显著提高了合金的力学性能,铸件的抗拉强度达到613MPa,屈服强度达到528 MPa,伸长率为6%。
Al-7.2Zn-2.2Mg-1.8Cu-0.2Zr and Al-7.2Zn-2.2Mg-1.8Cu-0.2Sc-0.2Zr two kinds of aluminum alloy were melted by resistance furnace and extruded at 700-720 ℃, And after 465 ℃ × 24h +475 ℃ × 8h water quenching + 120 ℃ × 24h aging heat treatment. The results show that the addition of Sc and Zr can remarkably refine the α-Al matrix and the interphase second phase. The mechanical properties of the alloy are improved obviously by multi-stage solution treatment and aging treatment. The tensile strength of the castings reaches 613 MPa, The strength reaches 528 MPa and the elongation is 6%.
其他文献
研究了电磁搅拌对Incoloy825高温合金凝固组织及凝固过程中溶质元素偏析的影响。结果表明,在合金凝固过程中,施加电磁搅拌能够有效细化晶粒组织,同时增加等轴晶比例。当电磁
在异步热线切割成型EPS模样技术中,由于传统二维CAD设计无法准确地描述三维实体,从而导致模型设计与加工存在偏差.利用Microsoft Visual Studio软件完成异步线切割加工装置的
提出了一种正交试验与灰色关联分析相结合的6005A铝合金板材MIG电弧焊工艺参数多目标优化方法。以试验数据为基础,将多工艺目标参数优化问题转化为对单一目标灰色关联度的优
对汽车发动机用AM50合金进行了Er合金化处理,研究了Er含量对AM50合金组织和耐腐蚀性能的影响。结果表明,Er微合金化AM50合金组织中除了含有α-Mg相和β-Mg17Al12相外,还形成
金属熔体外场处理技术是金属熔体处理技术的重要类别之一,它应用于金属半固态或低温液态流变成形等各种铸造场合,目的是实现凝固组织的整体均匀化和细化。基于性价比,提出了
通过ProCAST软件对一种GIS用壳体的原铸造工艺进行充型与凝固仿真分析,研究了该零件出现的铸造缺陷的原因,并进行了工艺优化。结果表明,大法兰面采用厚25mm的随型冷铁,其工艺
铸造企业引入ERP系统能有效管控生产制造过程。对于已经实施财务供应链系统的企业,就如何实现双系统集成,成了铸造企业信息化进程中亟待解决的问题。双ERP系统之间业务和数据
为评判金属及其合金的挤压铸造充型能力、开裂敏感性和补缩能力3个主要的挤压铸造工艺性能,分别定义了极限充型长度、极限留模时间以及有效补缩距离3个指标,给出了这些表征量
根据泵体零件的结构特点,设计了浇注系统、排溢系统和压铸工艺参数。用ProCAST软件进行了充型凝固过程数值模拟,根据模拟结果改进了浇注系统,确定了合理的压铸工艺参数:浇注
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥