A novel-type delivery system consisting of a special feeding device and delivery device was developed and applied to a f 600 mm×1 000 mm twin-roll casting system for producing the steel strip of 2 mm in thickness,and the characteristics of fluid flow and temperature field in the casting pool were investigated by mathematical simulation.The results showed that the melt from the novel-type delivery system was distributed to the casting pool along the width direction smoothly and uniformly.At the casting speed of 80 m/min,the difference of minimum residence time(tmin) and actual average residence time(tave) among different ports of the delivery device was less than 0.18 s and 0.26 s respectively,and the average amplitude of level fluctuation was 0.3 mm to 0.6 mm on the free surface of casting pool.In addition,the difference of temperature on the free surface of the pool was below 20 K and the difference across the width direction of roll in different pool depths was less than 13 K,which indicates that the uniformity of temperature distribution was obtained in the casting pool to maintain the casting process and the defect-free steel strip can also be obtained. A novel-type delivery system consisting of a special feeding device and delivery device was developed and applied to af 600 mm × 1000 mm twin-roll casting system for producing the steel strip of 2 mm in thickness, and the characteristics of fluid flow and temperature field in the casting pool were investigated by mathematical simulation. The results showed that the melt from the novel-type delivery system was distributed to the casting pool along the width direction smoothly and uniformly. At the casting speed of 80 m / min, the difference of minimum residence time (tmin) and actual average residence time (tave) among different ports of the delivery device was less than 0.18 s and 0.26 s respectively, and the average amplitude of level fluctuation was 0.3 mm to 0.6 mm on the free surface of casting pool. In addition, the difference of temperature on the free surface of the pool was below 20 K and the difference across the width direction of roll in different pool depths was less than 13 K, which indicates that the uniformity of temperature distribution was obtained in the casting pool to maintain the casting process and the defect-free steel strip can also be obtained.