【摘 要】
：
The mechanical and thermal properties of steel reinforced concrete columns with CFRP reinforcement were examined after exposure to a high temperature of 500℃. The concrete made with normal and recycled coarse aggregate (RCA) was fabricated and three diffe
【机 构】
：
Institute for Disaster Management and Reconstruction, Sichuan University, Chengdu 610207, China;Fail
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The mechanical and thermal properties of steel reinforced concrete columns with CFRP reinforcement were examined after exposure to a high temperature of 500℃. The concrete made with normal and recycled coarse aggregate (RCA) was fabricated and three different RCA replacement ratios (0, 50％, and 100％) were investigated. The fatigue properties of steel reinforced concrete with RCA and CFRP reinforcement were tested for two million cycles at a frequency of 2.5 Hz. The test results show that the failure of strengthened specimens is mainly caused by rupture of CFRP jacket and buckling of inner section steel reinforcement. However, for the unstrengthened specimen, both of inner steel buckling and core concrete cracking are the main contributors to the damage. The load-bearing capacity, deformation and energy dissipation of the specimens during the fatigue test could be strengthened greatly by CFRP reinforcement. However, the CFRP reinforcement has little influence on the improvement of the stiffness of the specimens, which may be caused by a plastic damage accumulation during the early cycles of fatigue tests. Finally, a static test was conducted on the postfatigue specimens, the results showed that a large decrease in stiffness was observed for the specimens subjected to high temperature and fatigue, and the fatigue loading had a higher influence on the specimens than the high temperature.
其他文献
A novel photosensitive copolymer P(SS-co-AA-g-GMA) (PSAG) was synthesized and utilized to noncovalently functionalize pristine single-walled carbon nanotubes (SCNTs). PSAG was highly effective for the solubilization of SCNTs in water and validated by UV-v
In order to improve the oxidation resistance of TiAl alloy,silicide coatings were prepared by pack cementation method at 1273,1323,and 1373K for 1-3 hours.Scanning electron microscopy (SEM),energy dispersive spectrometry (EDS) and X-ray diffraction (XRD)
To study the extraction difficulty of lithium ions from various crystal planes of Li2TiO3,according to the first principle,four representative crystal surfaces of Li2TiO3(precursor),(-133),(-206),(002) and(-131),were selected to establish a model and to c
The pastes containing different dosages of fly ash were taken into ultraviolet radiation and low temperature freeze condition simultaneously(URL) for 30 days and only ultraviolet radiation condition(UR) for 30 days after standard curing,so as to investiga
Taking dodecanethiol as the representative, we investigated the corrosion inhibition perfor-mance of SAL in seawater under pressures from 0.1 to 9 MPa. By using scanning Kelvin probe, the dodeca-nethiol SAL is confirmed to build on Cu surface, and the mod
To develop an efficient and bio-compatible way to improve the thermal and mechanical properties of addition type liquid silicone rubber (LSR),a series of modified LSR samples were prepared by introducing octavinyl-polyhedral oligosilsesquioxanes (VPOSS) a
To efficiently utilize the kaolin, an economical way of preparing cordierite ceramic with high performance for electric heater supports was put forward. In this study, sintering process, phase transformation, microstructure evolutions were systematically
A new type of capric acid (CA)-acid expanded vermiculite (AEV) composite phase change material (PCM) with improved adsorption ability and interface adhesive strength was developed. Through the analysis of non-isothermal phase transition kinetics, modified
The isothermal absorption properties and kinetic model of Cr (Ⅵ) and Cr (Ⅲ) onto ettringite were investigated using the batch adsorption method. IR analysis was used to study the difference and mechanism of the adsorption of chromium ions with different v