【摘 要】
：
To further improve the metallurgical quality of electroslag remelting, remove the large inclusions in electroslag ingot and refine the solidification structure of electroslag ingot, an electroslag remelting furnace with electromagnetic stirring was design
【机 构】
：
School of Metallurgy Engineering,Anhui University of Technology,Ma’anshan 243002,Anhui,China;Anhui F
论文部分内容阅读
To further improve the metallurgical quality of electroslag remelting, remove the large inclusions in electroslag ingot and refine the solidification structure of electroslag ingot, an electroslag remelting furnace with electromagnetic stirring was designed, and the influence of different magnetic induction intensities on metallurgical quality of GCr15 electroslag ingot was studied. Inclusions with different sizes and types were analyzed by an ASPEX scanning electron microscope, and the morphology and composition of inclusions were further observed by a JSM-6510LV scanning electron microscope. The distribution of alloying elements on the cross section of electroslag ingot was analyzed by original position analysis (OPA). The results show that whether or not electromagnetic stirring is used, the inclusions in electroslag ingot are mainly composed of Al2O3, MnS, MnS-oxide and other oxides, among which Al2O3 is the most. Compared with an electroslag ingot without electromagnetic stirring, the number of inclusions decreases considerably, and the proportion of small inclusions increases while the proportion of large inclusions decreases when the electromagnetic stirring with remelting current of 1.1 kA and magnetic induction intensity of 62 Gs is applied. However, excessive electromagnetic force will cause the number and diameter of inclusions to increase again. Electromagnetic stirring has different effects on the segregation of different elements. Under the experimental conditions, the weak electromagnetic force with 1.1 kA and magnetic induction intensity of 108 Gs has little effect on the segregation of C, but decreases the segregation of P, and the excessive electromagnetic force aggravates the segregation of alloy elements.
其他文献
近年来,脱发人群占比越来越大,而雄激素性脱发作为其中最常见的一种类型,病因复杂,治疗药物单一,且副作用大.为了能更好的研发治疗雄激素性脱发的药物,现对近年来有关雄激素性脱发相关靶点研究现状进行总结.归纳针对每个靶点所开发的药物及其副作用,旨在更全面地了解治疗雄激素性脱发的可能成药靶点,对后续研发新药起到一定的指示作用.综述可见雄激素受体仍然是新药研发的热门靶点;前列腺素作为近年来的新靶点,其药物开发主要还是采用“老药新用”的策略;多靶点药物的前景良好.
肉毒毒素是肉毒梭状杆菌在生长复制过程中所产生的一种嗜神经毒素.随着对肉毒毒素作用机制的不断探索,其应用领域日益广泛.近年来,A型肉毒毒素治疗雄激素性脱发所取得的显著效果受到了学者们的广泛关注,但其作用机制、疗效及安全性尚未明确.笔者通过查阅国内外相关文献,系统回顾了雄激素性脱发的发病机制及研究现状,并纳入6项关于A型肉毒毒素治疗雄激素性脱发的临床试验研究.现就A型肉毒毒素治疗雄激素性脱发的机制及研究进展作一综述,从而对A型肉毒毒素治疗雄激素性脱发的有效性和安全性做出系统评价.
目的 观察自体脂肪移植联合A型肉毒毒素注射在面部年轻化中的应用效果.方法 自2018年5月至2020年6月,南充市中心医院烧伤整形美容外科将60例面部老化的患者,随机分为观察组与对照组(30例/组),两组均进行自体脂肪移植,制备nanofat填充眶周凹陷,脂肪颗粒填充面部其余凹陷处,观察组在自体脂肪移植结束同期行全面部A型肉毒毒素皮内注射(25 U).观察两组患者术后皮肤、轮廓改善状态及不良反应.结果 观察组皮肤指标、轮廓改善评分与对照组比较,差异有统计学意义(P<0.05),观察组满意度高于对照组(P<
The total content of Al and Ti in advanced Ni-based wrought superalloys is up to 7.5wt.％, which makes it easier to form harmful nonequilibrium eutectic (γ+γ\') and η phase. It has been reported that the addition of certain amount of Zr can modify precip
乡村振兴战略的提出,为我国村镇建设提供了发展方向.文章以广西容县黎村镇为例,论述乡村振兴背景下我国小城镇的产业规划设计,并结合自身条件,分析村镇如何改善提高产业结构,依次提出产业目标、产业布局与规划实施措施,希望改善现状的发展困境,为我国村镇未来发展提供一定的参考.
以上海新场中学综合整新工程为例,结合新时期中小学校舍修缮的新要求,梳理综合整新工程的特征及实施过程中面临的主要难点,提出解决方法与管理的关键要点;进而对新时期中小学校舍修缮工程的实施与管理提出思考与建议.
目的 探讨眶隔法重睑成形术处理肿泡眼的临床效果.方法 2019年1—12月,湖南省人民医院整形激光美容科对121例肿泡眼患者,先按常规法行切口设计并画线,按设计线去除多余的皮肤、眼轮匝肌和肌肉下脂肪,显露眶隔;切口下方保留肌皮瓣,去除疏松脂肪筋膜,保留致密的睑板前筋膜;切口上方沿肌肉缘横向剪开眶隔,去除膨出的眶隔脂肪,修薄肌肉下脂肪层;将剪开眶隔的下部以其与上睑提肌腱膜的融合处为蒂,向下翻转下置,与下方眼轮匝肌上缘及其后方睑板前筋膜缝合固定;缝合皮肤、肌肉、眶隔(睑板前筋膜)、肌肉、皮肤.结果 本组121
文章选取豫东地区典型农村住宅为研究对象,对农村住宅节能改造进行研究.首先,基于绿建斯维尔节能设计软件,运用参变法对研究对象进行能耗模拟分析,并提出多个节能改造方案;然后,综合施工工艺、造价等相关因素,对节能改造方案进行优选,并对优选方案进行验证.结果显示,最终的优选方案可行、可靠,对豫东地区农村住宅的节能改造具有理论和指导意义.
面部脂肪移植后3D测量评估体积有助于更客观地了解脂肪移植的成活率,若将其合理运用,术前可以辅助分析面部存在缺陷的部位、预测注射量,客观评价术后效果,提高相关研究结果的客观性及可信度.现将近年来面部3D测量评估方法作一综述,总结3D测量评估在面部脂肪移植领域的应用方式和效果,梳理了国内外面部脂肪移植研究中3D测量的应用,并对面部脂肪移植客观评估方法进行了分类和评价,以更好地将3D测量评估应用于面部脂肪移植领域的临床和科研领域.
目的 探讨提上睑肌高位前徙术治疗中重度上睑下垂的临床效果.方法 自2018年6月至2020年10月,潍坊医学院整形外科研究所收治中重度上睑下垂患者53例,均行提上睑肌高位前徙术治疗.自眶隔后壁及提上睑肌腱膜间疏松组织分离至Whitnall氏上部横韧带,切断提上睑肌腱膜-米勒氏肌;然后向上分离,形成一个游离矩型瓣,缝合于睑板上,使提上睑肌腱膜形成瓦合样结构;嘱患者睁眼观察效果,效果满意后缝合.结果 53例患者获随访6～18个月,术后上睑均矫正到满意位置,双侧对称,无闭合不全、成角畸形、暴露性角膜炎等并发症发