【摘 要】
：
The phase constitution in mixed Gd2O3 and B4C by sintering in graphite tube furnace at the temperature of 100～1489 ℃ in argon atmosphere was studied by means of
【机 构】
：
School of Material and Metallurgy
论文部分内容阅读
The phase constitution in mixed Gd2O3 and B4C by sintering in graphite tube furnace at the temperature of 100～1489 ℃ in argon atmosphere was studied by means of XRD and TG-DTA. The results show that the impurity C reacts with O in the B4C at the temperature of 367～458 ℃. When the temperature is 800 ℃, Gd2O3 reacts with B4C, and the reaction products include GdB6, GdB4, GdBO3, GdBC and B. GdBC changes into GdB4 at 1200 ℃. When the temperature is 1470 ℃, GdB6 is obtained by the reaction of GdB4 with elemental B. The content of GdB6 is increasing with the prolonging time.
其他文献
The anodic films of novel Pb-Ca-Sn-Ce alloy, traditional Pb-Ca-Sn and Pb-Sb alloys formed in sulfuric solution at anodic +0.9 V potential corrosion for 6 h were
The syntheses of three nonlinear reverse saturation absorption compounds-Indanthrone and its two derivatives are discussed. The properties of nonlinear reverse
A support vector machine (SVM) with quadratic polynomial kernel function based nonlinear model one-step-ahead predictive controller is presented. The SVM based
The physical and thermal properties of P2O5-Al2O3-BaO-La2O3 glasses were investigated. The effects of glass compositions on the transition temperature, thermal
In order to estimate the feasibility of electromagnetic casting (EMC) for different metals, a mathematical model named the electromagnetic dimensionless number
研究RoHS指令中金属、非金属样品中六价铬消解的方法、步骤、注意事项.探索研究金属样品六价铬消解的最适条件及非金属消解的基本步骤,解决消解含六价铬样品的疑难问题.
通过对典型代表的200户居民和50处办公室的室内空气检测后发现宁波市的室内空气污染不可忽视。其中甲醛超标率分别为60．3％和36．0％，TVOC超标率率分别为33．8％和19．0％，苯系物超标率为5．0％左
Surface tension and filling ability of molten metal play an important role on the shaping of the molten metal. The surface tension was calculated from wetting a
La0.8 Cu0.2 MnO(3±δ) perovskite-type catalyst for methane combustion prepared through sol-gel process was characterized by X-ray Diffractometry(XRD), X-ray Ph
A nanostructured surface layer was fabricated on 1420 aluminum alloy by high-energy shot peening.Microstructures were characterized by X-ray diffractometer (XRD