Development of burn-resistant titanium alloys is the most direct way of mitigating the ignition and propagation of titanium fires in jet engines. WSTi3515S alloy(Ti–35V–15Cr–0.3Si–0.1C) is a new high alloying beta type burn-resistant titanium alloy, belonging to Ti–V–Cr type alloys which have been made significant progress in engineering technology in the past 5 years. The physical properties of WSTi3515S burn-resistant titanium alloy such as the elastic properties and thermal properties were measured and analyzed in different conditions. The results show that both the Young’s modulus and shear modulus of WSTi3515S alloy decrease slightly with the temperature increasing at the tested temperature range. The Poisson’s ratio of WSTi3515S alloy is around 0.36. However, the thermal properties such as the specific heat, thermal diffusivity, thermal conductivity and thermal expansion increase with the temperature increasing, which results from the strengthening of lattice heat vibration at elevated temperature. And the room temperature density of WSTi3515S alloy is 5.295 gácm~(-3).
Development of burn-resistant titanium alloys is the most direct way of mitigating the ignition and propagation of titanium fires in jet engines. WSTi3515S alloy (Ti-35V-15Cr-0.3Si-0.1C) is a new high alloying beta type burn-resistant titanium alloy, belonging to Ti-V-Cr type alloys which have been made significant progress in engineering technology in the past 5 years. The physical properties of WSTi3515S burn-resistant titanium alloy such as the elastic properties and thermal properties were measured and analyzed in different conditions. The results show that both the Young’s modulus and the shear modulus of WSTi3515S alloy decrease slightly with the temperature increasing at the tested temperature range. The Poisson’s ratio of WSTi3515S alloy is around 0.36. However, the thermal properties such as the specific heat, thermal diffusivity, thermal diffusion and increase with the temperature increasing, which results from the strengthening of lattice heat vib ration at elevated temperature. And the room temperature density of WSTi3515S alloy is 5.295 gácm ~ (-3).