A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2SO4/K2SO4(3:1) or Na2SO4/NaCl(3:1) salts at 900 °C in static air are evaluated as well as the aluminide coating.The results indicate that compared with the aluminide coating,the anti-corrosion properties of the Cr-modified aluminide coating in the both salts are improved,which should be attributed to the beneficial effect of the Cr in the coating.The corrosion mechanism of the Cr-modified aluminide coating,especially the role of Cr in the mixture salt corrosion,is discussed.
A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing. Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2SO4 / K2SO4 (3: 1) or Na2SO4 / NaCl ( 3: 1) salts at 900 ° C in static air are evaluated as well as the aluminide coating. The results that compared with the aluminide coating, the anti-corrosion properties of the Cr-modified aluminide coating in the bottle salts are improved, which should be attributed to the beneficial effect of the Cr in the coating. The corrosion mechanism of the Cr-modified aluminide coating, especially the role of Cr in the mixture salt corrosion, is discussed.