Steel slag which is mainly composed of γ-Ca2SiO4 and other silicates or alumino-silicates is activated by sodium silicates and sodium hydroxide. The powders of such steel slag are usually inert to hydrate and subsequently have very low ability of ce- menting. But when sodium silicates and sodium hydroxide are used as activators the steel slag shows very good properties of ce- menting. When activated with NaOH solution the hardened slurry of the steel slag has a compressive strength of 11.13 MPa after being cured for 28 days. When activated with Na2SiO3 solution the samples after being cured for 28 days have an average compres- sive strength of 40.23 MPa. While the steel slag slurry which is only mixed with water has a compressive of 0.88 MPa after being cured for 28 days.
Steel slag which is mainly composed of γ-Ca2SiO4 and other silicates or alumino-silicates is activated by sodium silicates and sodium hydroxide. The powders of such steel slag are usually inert to hydrate and subsequently have very low ability of ce- menting. But when When activated with NaOH solution the hardened slurry of the steel slag has a compressive strength of 11.13 MPa after being cured for 28 days. When activated with sodium hydroxide are used as activators the steel slag shows very good properties of ce- menting. Na2SiO3 solution the samples after being cured for 28 days have an average compres sive strength of 40.23 MPa. While the steel slag slurry which is only mixed with water has a compressive of 0.88 MPa after being cured for 28 days.