【摘 要】
：
用硬度、室温拉伸和电镜观察等方法研究了时效处理对快速凝固 Al-8.23Fe-3.62Ce 合金结构及性能的影响。研究发现,在573K 时效6h,合金中无明显的沉淀析出和相长大.时效30h,其
【机 构】
：
中国科学院金属研究所,中国科学院金属研究所,中国科学院金属研究所,中国科学院金属研究所 沈阳市 110015
论文部分内容阅读
用硬度、室温拉伸和电镜观察等方法研究了时效处理对快速凝固 Al-8.23Fe-3.62Ce 合金结构及性能的影响。研究发现,在573K 时效6h,合金中无明显的沉淀析出和相长大.时效30h,其抗张强度不降低。在高于673K 的温度下长期时效,沉淀相很快脱溶并聚集长大,导致合金室温强度降低。
The effects of aging treatment on the structure and properties of rapidly solidified Al-8.23Fe-3.62Ce alloy were investigated by hardness, tensile at room temperature and electron microscopy. The study found that, at 573K aging 6h, the alloy precipitation and precipitation did not significantly large, aging 30h, its tensile strength does not decrease. Long-term aging at a temperature higher than 673K, the precipitated phase quickly dissolves and aggregates and grows, resulting in a decrease in the room temperature strength of the alloy.
其他文献
In this paper,a class of singular perturbation of noidocal boundary value problems forelliptic partial differentia[ equations of higher order is considered by u
随着铁路、水利、矿山等工程的发展,越来越多的硐室需要在深部开挖。工程爆破开挖和断层滑移等动力荷载严重影响着地下硐室围岩的稳定性。利用有限差分软件FLAC3D,对地下硐室
根据Moley的界面守恒原理而推导出的19条矿石单体解离定理,解决了二相系统单体解离过程中的含量分布问题。由于是以球形粒子来考虑的,因而对于实际发生的破碎颗粒必须考虑其
为研究地铁装配式外置槽道在火灾场景下的安全性能,采用ABAQUS有限元软件建立混凝土管片、纵向连接螺栓以及外置槽道的数值模型,模拟计算其在碳氢(HC)升温曲线下的温度与温度
以定向反应合成的 YBa_2Cu_3O_x 为原料,用加大成型压力——高温熔化——三段热处理工艺,可将 YBa_2Cu_3O_x 体材料的 J_c 提高到 713 A/cm~2(78 K);讨论了晶粒间界的空隙,微
含1.5%W 的 Fe-Cr-Co-V-Ti 永磁体,是 Fe-Cr-Co 系永磁材料中的一个新品种。本文研究了该合金的剩余磁感稳定性、得到温度、外磁场、铁磁物质、时间和冲击力对磁性的影响规律
非晶态Fe_(1-x)(Si,B)_x合金的磁矩和磁致伸缩随着Si和B含量的增多而缓慢降低,而Curie温度约在25%(Si+B)含量时呈现出最大值;Si与B的含量对磁各向异性并无明显影响,但表面条
5G开启正式商用之后,媒体机构、通信运营商、终端品牌等都在持续加码战略布局,以BAT为代表的互联网机构自然也不会甘于人后。一方面,互联网机构希望利用5G大带宽、高速率、低
如今的你： 你好！ 如今的你在幼稚中多了一份成熟，感性中多了一份理智，活泼中多了一份淡然，但对于现在的你我还想说点什么。 如果你是一片落叶，我希望你能以最美的姿态落下，莫要让别人看到你背后的忧伤;如果你是一朵梅，我希望你能勇敢地在寒冬绽放，哪怕在凋零之时也可以让别人闻到你的芬芳;如果你是一抹暖阳，我希望你能在风雨来临之前给自己多藏些暖意，好照亮你的心房。或许这世上的美都有一些苍凉，但你要学会
一、前言 Fe-Mn基合金由于在低于反铁磁转变点T_N产生因瓦和埃林瓦效应,加之该类合金不含或少含贵重稀缺元素,在研制无磁低膨胀和无磁恒弹性合金中一直受到重视。在合金成分