The adsorption amount of poly(styrene sulfonate)and poly(dimethyldiallyl ammonium chloride)(PSS/PDDA) self-assembled multilayer membranes in designed dipping solvents were measured by UV-Vis-spectroscopy and quartz crystal microbalance(QCM).Intrinsic viscosities of PSS and PDDA in corresponding dipping solvents were determined by an Ubbelohde viscometer.It is found that the adsorption amount of PSS/PDDA self-assembled multilayer membranes built up in different dipping solutions,added salt concentration,pH of solution and solvent quality,respectively changed oppositely with the corresponding intrinsic viscosity of PSS and PDDA in dipping solvents.A negative relation between the adsorption amount and intrinsic viscosity was revealed,and explained in term of the concept of excluded volume of polymer molecule in dilute solutions.
The amount of poly (styrene sulfonate) and poly (dimethyldiallyl ammonium chloride) (PSS / PDDA) self-assembled multilayer membranes in designed dipping solvents were measured by UV-Vis-spectroscopy and quartz crystal microbalance (QCM) and PDDA in corresponding dipping solvents were determined by an Ubbelohde viscometer. It is found that the amount of deposition of PSS / PDDA self-assembled multilayer membranes built up in different dipping solutions, added salt concentration, pH of solution and solvent quality, respectively changed oppositelyly with the corresponding intrinsic viscosity of PSS and PDDA in dipping solvents. A negative relation between the adsorption amount and intrinsic viscosity was revealed, and explained in term of the concept of excluded volume of polymer molecule in dilute solutions.