【摘 要】
：
We developed flexible and transparent thin film heaters (TFHs) with a structure of AZO/Ag-SnOx/AZO/Polyimide (PI) which exhibited superior stability under opera
【机 构】
：
School of Materials Science and Engineering,Shanghai University,Shanghai 200444,China;Ningbo Institu
论文部分内容阅读
We developed flexible and transparent thin film heaters (TFHs) with a structure of AZO/Ag-SnOx/AZO/Polyimide (PI) which exhibited superior stability under operational conditions.Ultrathin and robust doped silver (Ag) films were produced by introducing a small amount of SnOx during the sput-tering process.The AZO/Ag-SnOx/AZO stacks showed the best figure of merit value of 139.9,which was higher than that of ITO counterpart (25.5) with the same thickness.In addition,it exhibited excellent durability,which showed unaffected optical and electrical properties under the heat treatment of 500 ℃for 30 min in air,highly-accelerated temperature and humidity stress test (HAST) at 121 ℃ and 97％ RH for 36 h,10,000 times of scratching and 1500 times of inner and outer bending test.Furthermore,the TFHs based on AZO/Ag-SnOx/AZO/PI achieved a high temperature of 438.8 ℃ with response time in several seconds,which outperformed most previous studies.The robust high-temperature TFHs in this research hold promising commercial applications in flexible and high temperature occasions.
其他文献
This work characterizes microstructural evolutions of electron beam melted (EBM) Ti-6Al-4V alloy mod-ified via laser shock peening (LSP).The depth stress distri
Doping in pristine 2D materials brings about the advantage of modulating wide range of mechanical properties simultaneously,However,intrinsic defects (such as S
Efficient charge carrler transfer from light harvesters to catalysts greatly determines the photocatalytic activity in an artificial photosynthesis (AP) system
As candidate thermal/environmental barrier coatings (T/EBCs),the structure characteristics and compre-hensive properties of monoclinic-prime (m') RETaO4 (RE =Yb
Chalcogenide based phase change random access memory (PCRAM) holds great promise for high speed and large data storage applications.This memory is scalable,requ
Austenite formation from a ferrite-cementite mixture is a crucial step during the processing of advanced high strength steels (AHSS).The ferrite-cementite mixtu
MgH2 is one of promising hydrogen storage materials due to its high hydrogen capacity of 7.6 wt％.However,MgH2 nanocrystallites easily grow up during hydrogen abs
Strong metal/non-polar plastic dissimilar joints are highly demanded for the lightweight design in many fields,which,however,are rather challenging to achieve d
The Portevin-Le Ch(a)telier (PLC) effect is a plastic instability in alloys at certain strain rates and deforma-tion temperatures.This plastic instability exhib