【摘 要】
：
Plasma electrolytic oxidation(PEO) processes were carried out to produce ceramic layers on 6061 aluminum substrates in four kinds of electrolytes such as silica
【机 构】
：
School of Nano & Advanced Materials Engineering,Surface Technology Research Center
论文部分内容阅读
Plasma electrolytic oxidation(PEO) processes were carried out to produce ceramic layers on 6061 aluminum substrates in four kinds of electrolytes such as silicate and aluminate solution with and without sodium fluorosilicate. The PEO processes were carried out under a hybrid voltage (260 V DC combined with 200 V, 60 Hz AC amplitude) at room temperature for 5 min. The composition, microstructure and element distribution analyses of the PEO-treated layers were carried out by XRD and SEM & EDS. The effect of the electrolyte contents on the growth mechanism, element distribution and properties of oxide layers were studied. It is obvious that the layers generated in aluminate solutions show smoother surfaces than those in silicate solutions. Moreover, an addition of fluorine ion can effectively control the layer porosity; therefore, it can enhance the properties of the layers.
其他文献
Al was prepared by a new method in molten salt at low temperature. Sintered alumina pellets were used as cathode; graphite rod was employed as anode; and the mo
A pipeline steel X80 with welded joint was subjected to surface mechanical attrition treatment (SMAT). After SMAT, a nanostructure surface layer with an average
Thermal spraying technique is widely used in various mechanical parts as a surface reforming technique. However, as demand to maintain superior mechanical perfo
Mesoporous titanium dioxide films were fabricated on titanium plates by micro-arc oxidation method.To increase the photocatalytic activity of the films,NH4NO3 w
A series of anodic aluminum oxide(AAO) was grown on the commercially pure 1050 aluminum sheet by controlling electrolyte temperature(2-15 ℃) and anodizing time
Thermal spray coating presents a sacrificial-anode cathodic protection method since differences between the potentials of materials are employed. If a base meta
The phase composition,magnetic properties i.e.coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 allo
The composite laminates with embedded acrylonitrile butadiene rubber (NBR) layer were fabricated by cocuring process. The embedded layers were perforated with a