对含预合金316L不锈钢和NH4HCO3(质量比96:4)的混合粉末进行选区激光熔化,制备多孔材料的实验研究。利用扫描电镜分析试样的微观孔隙特征。结果表明,在较高激光功率(800W)条件下,可形成蜂窝状的多孔结构,孔径分布均匀(2~5μm),平均孔径约3.5μm。分析激光功率对多孔结构特征的影响,讨论选区激光熔化蜂窝状多孔结构的形成机制。
Experimental study on the preparation of porous materials by selective laser melting of mixed powders containing 316L stainless steel and NH4HCO3 (mass ratio 96: 4). The microscopic pore characteristics of the samples were analyzed by scanning electron microscopy. The results show that under the condition of high laser power (800W), honeycomb porous structure can be formed with uniform pore size distribution (2 ~ 5μm) and average pore size of about 3.5μm. The influence of laser power on the characteristics of porous structure was analyzed, and the formation mechanism of laser melted honeycomb porous structure in selective area was discussed.
其他文献
铸造-倾析-铸造技术是近年来发展起来的一种制备功能梯度材料的新方法。采用这种方法制备在径向具有梯度功能的圆柱形试样，其外表层为具有高耐磨性的 A390铝合金，芯部为具有较
使用分子动力学方法模拟PbAu、PbAu和PbAu 3种合金的热力学性质,计算合金的过剩自由能、结合能和形成能等能量方程.结果显示:合金的形成能和过剩自由能均为正值,因此Pb-Au合
Blind equalization based on adaptive forgetting factor, recursive least squares (RLS) with constant modulus algorithm (CMA), is investigated. The cost function
在温度T=250~450℃,应变速率为0.001~10s-1的条件下,利用Gleeble-3500热模拟试验机对挤压Mg-7.8%Li-4.6%Zn-0.96%Ce-0.85%Y-0.30Zr合金进行高温热压缩试验,分析流变应力曲线
根据TiAl基合金片层组织的准三维金相形态准确地判断出其初生相类型.结果表明,具有不同片层取向的晶粒在Ti-50Al-5Nb合金定向凝固过程中其初生相均为β相.
[目的]研究污灌土壤有机提取物对原代大鼠肝细胞DNA的损伤.[方法]选取A、B、C 3类污灌农田土壤为研究对象,地下水灌溉的土壤D为对照,采用超声振荡法提取土壤中的有机污染物,
In this paper, we investigate the performance of adaptive modulation (AM) orthogonal frequency division multiplexing (OFDM) system in underwater acoustic (UWA)
在不同温度下对Nd0.75Mg0.25(Ni0.8Co0.2)3.8储氢合金进行磁场热处理,分别对合金的电化学性能、磁性能、合金的相组成及点阵参数进行测试和计算.结果表明:合金在磁场热处理前
采用先进的放电等离子烧结技术(SPS)制备Ni-7W(at%,下同)(Ni7W)合金初始锭,通过高能球磨使Ni、W粉末充分混合,优化冷轧和热处理工艺制备出高立方织构的Ni7W合金基带。基带晶