我厂电镀小组在1964—1971年间一直是采用氰化物镀铜工艺,排出的有毒废水、废气和缸脚危害极大,严重影响职工身体健康。1673年虽也进行了无氰镀铜工艺试验,但是由于路线不端正,一遇到挫折,就止步不前了,致使几种配方逐渐被淘汰,总不能坚持下来,仍以镀镍代铜1976年初,电镀小组全体同志在党委的正确领导下,坚持“鞍钢宪法”精神,组成了三结合无氰电镀攻关小组,对焦磷酸盐镀
Our plating team in 1964-1971 has been using cyanide copper plating process, the discharge of toxic waste water, exhaust gas and cylinder foot great harm to the health of workers seriously. Although the process of cyanide-free copper plating was also carried out in 1673, due to the unjustified route, once the setback was encountered, it was halted. As a result, several formulations were gradually eliminated and could not be persevered. At the beginning of the year, under the correct leadership of the party committees, all the electroplating group comrades insisted on the spirit of the Anshan Iron and Steel Constitution, formed the three combined cyanide-free electroplating research team,