【摘 要】
：
采用TIG点焊工艺,搭接形式,制备了弹簧触指零件试样,并对试样进行了分析。结果表明,焊点组织与基材组织接近;热处理后焊点的抗拉强度达到800MPa,约为基材的93%;焊点硬度(HV)
论文部分内容阅读
采用TIG点焊工艺,搭接形式,制备了弹簧触指零件试样,并对试样进行了分析。结果表明,焊点组织与基材组织接近;热处理后焊点的抗拉强度达到800MPa,约为基材的93%;焊点硬度(HV)为420,与基材相当;电阻率约为0.069 9×10-6Ω·mm2/m,导电性能优于传统焊接方法。
Using TIG spot welding technology, lapped form, the spring contact finger parts were prepared, and the samples were analyzed. The results show that the microstructure of the solder joint is close to that of the substrate. The tensile strength of the solder joint after heat treatment reaches 800MPa, which is about 93% of the substrate. The hardness of the solder joint (HV) is 420, equivalent to that of the substrate. The resistivity is about 0.069 9 × 10-6Ω · mm2 / m, the conductivity is better than the traditional welding method.
其他文献
目的了解2009~2013年北流市人民医院护理论文发表状况。方法对2009~2013年北流市人民医院发表的186篇护理论文进行回顾性统计分析。结果论文发表作者中以40~49岁,大专文化,主
目前县级林业测绘主要使用工具为手持GPS,把现场实测的数据录入到电脑Arcgis系统中进行点、线、面的编辑,最终完成准确的测绘地图。为了让林业测绘更加简单方便,研究通过克服
根据目前对带式输送机的发展需求,设计了一种能够满足带式输送机对于张紧力和动态响应要求的自动张紧绞车装置。并且对其机械和液压结构、工作原理以及控制流程等方面分别进
从培养基和环境条件两方面入手,分别以1/2 MS和1/2 F14为基本培养基,添加不同浓度IBA,筛选出适宜ZY-1生根的培养基为：1/2 MS＋IBA 0.5 mg/L,平均生根率达91.2%,平均生根3.73条,
目的:通过建立大鼠心脏低电压损伤模型,观察低电压对大鼠心脏损伤的心肌酶学、心电图的变化,并分析心肌组织形态学变化,观察磷酸肌酸钠和舒血宁注射液(以下简称舒血宁)对大鼠
民俗是一种群众性的文化创造成果,是一定的社会群体在历史发展进程中,为应付各种环境、满足各种需要而不断积累起来的一种社会创造物,是没有个人版权所有的群众文化积淀.它具
利用工作船站1998-2008年逐日表层含沙量和短期水沙观测资料，分析了洋山深水港区海域的含沙量分布特征，提出适用于其他海域的年平均含沙量推算方法。分析表明：受长江入海泥沙减
20世纪20年代对肖像画问题的讨论不断深入.在1926-1927年间国立美术学院哲学部举行了委员会会议专门研究艺术哲学问题,会议公开并讨论了一系列文章,发表在加布里切夫斯基（А.
<正>对学生来说,毕业是一个令人激动的节日,是一个阶段的结束,也是另一个阶段的开始。所以学生把"毕业"二字看得很重,对毕业充满了期待与幻想。但对于现在的中学生来说,面对
<正>综合性学习课程的设置,对新课标下的义务教育语文教学内容来说,是一项重大改革,语文综合性学习是人教版初中语文课文中十分重要的一个组成部分,开展专项的综合性学习研究