【摘 要】
：
Nano SiO2 was filled into gypsum particleboard. Effect of the amount of nano SiO2 particles filled,ultrasonic dissipating duration and treating the nano particl
【机 构】
：
College of Information Science and Technology,College of Wood Science and Technology,College of Mech
论文部分内容阅读
Nano SiO2 was filled into gypsum particleboard. Effect of the amount of nano SiO2 particles filled,ultrasonic dissipating duration and treating the nano particles with different coupling agents on the mechanical properties of the board were studied respectively. The results show that nano SiO2 is helpful for the improvement of the properties. Adding 3%(mass fraction) nano SiO2 is the best for the improvement of both modulus of rupture(MOR) and modulus of elasticity(MOE) of the boards formed at 30 ℃ or 40 ℃. For the boards formed at 30 ℃,their MOR and MOE can be improved by 8.77% and 12.24%,and MOR and MOE of the boards formed at 40 ℃ can be improved by 44.44% and 108.38%.3% is also the best addition proportion to improve internal bond(IB) of the boards formed at 30 ℃,while 5% is the best for that of the boards formed at 40 ℃. At room temperature,dissipating nano SiO2 into flake by ultrasonic has better effect on the properties of the final products. Through ultrasonic treating for 1 h and the best treating duration,the MOR and MOE can be increased by 41.99% and 47.80%. In addition,different coupling agents have different effects on the final properties too,and silane coupling agent KH570 is better for the improvement of properties of the boards formed at room temperature.
其他文献
The oxidation of two two-phase ternary Fe-Cu-Al alloys containing about 5%(mole fraction) aluminium, one Fe-rich and one Cu-rich, has been studied at 900 ℃ in
Sn-Al-P-B composites were synthesized by novel rheological technique. The microstructure, morphology, and electrochemical performance of the materials were inve
Microarc oxidation(MAO) coatings were prepared on the surface of aluminum alloys with different contents of magnesium. The morphologies and surface roughness of
Key variable identification for classifications is related to many trouble-shooting problems in process industries. Recursive feature elimination based on suppo
Extrusion is the key technology to manufacture aluminum profiles and involves complicate metal deformation coupled with temperature changes. The choice of numer
The effect of evolution of polycrystalline texture on normal anisotropy coefficient r-value of aluminum alloy sheet was investigated. For this purpose, the text
The fly ash was added to melt to increase the melt viscosity. The main components are quartz and mullite in the fly ash,therefore its a kind of hardness ceramic
The semi-solid slurry of A356 Al alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature on the sl
ZnSe∶Mn nanocrystals were grown by chemical vapour transport method using the matrix of SiO2 aerogels. The cubic structure of the nanocrystals was confirmed by
This study is to reveal the effect of interlayer lattice registry on the formation of collapsed double wall carbon nanotubes (DWCNTs). It is found that collapse