论文部分内容阅读
Ti(C,N) was synthesized with the starting materi-als of 76.9% titania white and 23.1% carbon black (graphite or activated carbon),or 40% titania white and 60% amylum,with or without 10% NaBr-KCI,dry moulding and carbon embedded firing at 1 300 ℃ and 1 400 ℃ for 3 h,respectively.Phase composition and microstructure of the synthesized Ti (C,N) were analyzed by XRD,SEM and EPMA.Effects of different carbon sources and NaBr-KCl on the synthesis of Ti (C,N) were investigated.The results show that:(1) Ti (C,N) can be synthesized by using carbon black,graphite,activated carbon or amylum as carbon source separately;(2) Additive NaBr-KCI is more fa-vorable for accelerating the carbothdrmal reduction reac-tion using carbon black or amylum as carbon source;(3) In the presence of NaBr-KCl,particle size of the synthesized Ti (C,N) is 5-8 μm using carbon black as carbon source fired at 1 300 ℃ for 3 h,while that is only 1-3 μm using graphite,activated carbon or amy-lum fired at 1 400 ℃ for 3 h.