The isothermal oxidation behavior of a Ti3Al-based alloy (Ti-24Al-14Nb-3V-0.5Mo-0.3Si, molar fraction, %) at 700- 1 000 ℃ in air was investigated. The oxidatio
【机 构】
：
R & D Center,Shenyang National Laboratory for Materials Science
论文部分内容阅读
The isothermal oxidation behavior of a Ti3Al-based alloy (Ti-24Al-14Nb-3V-0.5Mo-0.3Si, molar fraction, %) at 700- 1 000 ℃ in air was investigated. The oxidation kinetics of tested alloy approximately obeys the parabolic law, which shows that the oxidation process is dominated by the diffusion of ions. The oxidation diffusion activity energy is 241.32 kJ/mol. The tested alloy exhibits good oxidation resistance at 700 ℃. However, when the temperature is higher than 900 ℃, the oxidation resistance becomes poor. The XRD results reveal that the oxide product consists of a mixture of TiO2 and Al2O3. Serious crack and spallation of oxide scale occur during cooling procedure after being exposed at 1 000 ℃ in air for 16 h. According to the analysis of SEM/EDS and XRD, it is concluded that the Al2O3 oxide forms at the initially transient oxidation stage and most of it keeps in the outer oxide layer during the subsequent oxidation procedure.
其他文献
Surface-treated MmNi3.55Co0.75Mn0.4Al0.3 alloy as negative electrode material of nickel-metal hydride battery was employed to improve the high-rate dischargeabi
Dynamic friction polishing (DFP) is one of the most promising methods appropriate for polishing CVD diamond film with high efficiency and low cost.By this metho
Olivine-structured pure LiFePO4 and doped Li(M, Fe)PO4 (M=La, Ce, Nd, Mn, Co, Ni) have been synthesized by a solvothermal method.X-ray diffraction and field emi
Environmental availability and profile characteristics of arsenic (As), cadmium (Cd), lead (Pb) and zinc (Zn) were studied in contaminated vegetable soils from
High undercooling up to 392 K was achieved in eutectic Ni70.2Si29.8 alloy melt by using glass fluxing combined with cyclic superheating.A small quantity of amor
Hydrided Mg-3Ni-2MnO2 composite powders were fabricated by reactive ball milling with hydrogen, and accumulative hydrogenation kinetics and temperature field of
Laves phase NbCr2 alloys with a composition of Nb-66.7Cr (molar fraction, %) were prepared by mechanical alloying and hot pressing. The microstructures and prop
Epitaxial YBCO superconducting films were deposited on the single crystal LaAlO3. (001) substrate by metal organic deposition method. All YBCO films were fired
The phosphor BaB8O13:Eu3+ were synthesized by solid-state reaction, and their luminescent properties were studied under 254 and 147 nm excitation. The excitatio
The amenability of a refractory ore to the extraction of gold and silver by cyanide leaching was investigated. Diagnostic leaching tests were also performed to