【摘 要】
：
We developed poly lactic-co-glycolic acid (PLGA) microspheres loaded with cefquinome and tested their effectiveness in a mouse model.The microspheres were prepared by optimizing several key parameters such as PLGA molecular weight,drug/polymer ratio,inter
【机 构】
：
School of Medicine and Pharmacy, Ocean University of China, Qingdao 266003, China;Agricultural Bio-p
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
We developed poly lactic-co-glycolic acid (PLGA) microspheres loaded with cefquinome and tested their effectiveness in a mouse model.The microspheres were prepared by optimizing several key parameters such as PLGA molecular weight,drug/polymer ratio,internal water volume and ethyl acetate.Drug loading efficiency,stability,in vitro release and tissue distribution in mouse were evaluated.The average particle size of the microspheres was 27.84 μm.The drug loading efficiency was 64.57％.The in vitro release of cefquinome from microspheres after 4 h was about 40％ compared with over 90％ for the drug alone.The concentration of cefquinome in lung reached 25 μg/g 0.25 h after injection,and kept at 10 μg/g 4 h after injection.However,the concentration of cefquinome was very low in other organs even 0.25 h after injection.In conclusion,Cefquinome-loaded PLGA microspheres are compatible as an effective lung-targeting drug delivery system and have a good sustained release efficacy.
其他文献
WO3 nanowires were fabricated by a hydrothermal method, which proceeded at 170℃ for 48 h in a solution containing C2H10N6H2SO4 as a dispersant and Na2WO4 as a starting material. The nanowires exhibit a well crystallized one-dimensional structure with 20 n
In order to look for the best proportion ofβ-tricalcium phosphate(β-TCP) and poly(lactide-co-glycolide) (PLGA) we fabricated porous compositesβ-TCP/PLGA scaffold using freeze-drying method. Morphological characterization using scanning electron microscopy
Ba0.65Sr0.35TiO3 (BST) nanocrystals doped with different concentrations of Er3+ ion were fabricated using sol-gel method. The structure and morphology of these BST nanocrystals were studied using X-ray diffraction (XRD), field emission scanning electron m
The feasibility of using coral reef sand (CRS) in Portland cement concrete is investigated by testing the mechanical property and microstructure of concrete. The composition, structure and properties of the CRS are analyzed. Mechanical properties and micr
Ti6Al4V substrates were anodized in a 0.5 mol/L H2SO4 solution at applied voltages of 90-140 V. A hydroxyapatite-titanium oxide (HA-TiO2) coating was then deposited on the anodized Ti6Al4V substrates via a hydrothermal-electrochemical method at a constant
Fe3O4-octadecyltrichlorosilane (Fe3O4-OTS) was synthesized and used to remove dyes in a competitive system. Fe3O4-OTS was prepared by slow hydrolysis of OTS in cyclohexane on the surface of Fe3O4 obtained through coprecipitation method. Scanning electron