【摘 要】
：
Al2O3-SiO2-TiO2-ZrO2 supported membranes were prepared by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist seve
【机 构】
：
School of Material Science and Engineering,School of Material Engineering
论文部分内容阅读
Al2O3-SiO2-TiO2-ZrO2 supported membranes were prepared by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al2O3, TiO2(anatase), Al2SiO5, and ZrO2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investigated by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the surface nanoscale topography and microstructure of composite ceramic membranes were also analyzed.
其他文献
为改善水质环境,对福建省龙江中下流进行补水效果实验。根据控制断面测得的水质浓度和流量数据,计算水污染物通量。使用该通量评估污染负荷,计算生态补水量。所得污染物通量良好地反映出流域污染状况,实验效果显著,河流水质达到了国家规定标准。
采用Zn元素部分替代易形成玻璃合金Mg65cU25Y10中的Cu元素,形成Mg65Cu20zn5Y10合金.添加Zn元素可显著提高合金的玻璃形成能力,通过熔体铜模浇铸可制备出直径为6 mm的Mg65Cu20
对爆炸复合双金属板LYl2/20g中角裂纹的疲劳扩展行为进行了实验研究和理论分析.结果表明,双层金属板的界面结合强度、界面相性能和体积分数及界面两侧材料的性能都对层合板角
The leaching kinetics in cyanide media of the silver contained in the Dos Carlos waste tailings at the City of Pachuca de Soto, Hidalgo State, Mexico were carri
以TiO2,Al,C,纳米ZrO2粒子为原料,利用燃烧合成-热压工艺制备了Al2O3-TiC-ZrO2纳米复合陶瓷.添加ZrO2可使Al2O3-TiC断裂方式由沿晶断裂转变为穿晶断裂.ZrO2纳米粒子弥散于基
用表面机械研磨对低碳钢板材进行表面处理,经X射线衍射及透射电镜分析表明,处理后的样品上已形成了纳米结构表层.用往复式摩擦实验机研究了处理后样品的摩擦磨损性.结果表明
对用混合合金法制备的Nd7.69Dy6.62Fe64.33Co14.83B6.53/Ga烧结磁体的磁性和微观结构进行了研究.结果表明:添加0.5%(质量分数)的Ga后,磁体的iHc由1232 kA/m升高到1819 kA/m,
Low-concentration methane(LCM) has been one of the biggest difficulties in using coal mine methane.And previous studies found that premixed combustion in porous
The synthesis and characterization of PEG-like macromolecular structures on Nitinol surface from tri (ethylene glycol) dimethyl-ether under ECR-cold-plasma cond
The magnetocaloric effect in the A-site doping colossal magnetoresistance material (La0.6Dy0.1)Sr0.3MnO3 was studied. From the measurement and calculation of is