【摘 要】
：
以巯基乙酸为稳定剂合成了CdSe量子点,利用X-射线粉末衍射(XRD)和透射电镜(TEM)对量子点结构进行了表征,粒径约为5 nm。以碳二亚胺为缩合剂将量子点与免疫球蛋白共价连接,光
论文部分内容阅读
以巯基乙酸为稳定剂合成了CdSe量子点,利用X-射线粉末衍射(XRD)和透射电镜(TEM)对量子点结构进行了表征,粒径约为5 nm。以碳二亚胺为缩合剂将量子点与免疫球蛋白共价连接,光谱实验结果表明CdSe量子点与免疫球蛋白有效结合,其荧光发射峰发生了红移,而半峰宽和发射强度没有明显变化。
CdSe QDs were synthesized by using thioglycolic acid as stabilizer. The structure of QDs was characterized by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The particle size was about 5 nm. Quantum dots were covalently linked to immunoglobulin by using carbodiimide as a condensing agent. The results of spectral experiments showed that CdSe QDs were effectively combined with immunoglobulin, and the fluorescence emission peak was red shifted, while the half-width and emission intensity were not obvious change.
其他文献
目的:采用反相高效液相色谱法测定香青兰中齐墩果酸和熊果酸的含量.方法:采用Kromasil C18柱(4.6 mm×250 mm,5μm),流动相甲醇-0.2％磷酸二氢钠(88:12),流速1.0 mL· min -,检
多相搅拌过程中常常根据临界搅拌转速表征搅拌效果。由于各种搅拌桨的功率准数不同,低临界转速的搅拌桨对应的搅拌功耗可能大于高临界转速的搅拌桨,因此,本文提出用临界功率
采用乙醇脱水生成气态乙烯,使用微型反应装置与色谱联用的方法对ZSM-5分子筛催化剂的性能进行评价,探讨了温度、进料速率对催化剂的活性和选择性的影响。结果表明,分子筛催化
以研究与Sr,Mg掺杂LaGaO3 (LSGM)电解质匹配的阳极材料为出发点,系统研究了Ge1-xTmxO2-δ(Tm=Cu,Mn,Fe)固溶体的晶体结构、热化学稳定性、电化学性能和单电池发电实验.柠檬酸
采用密度泛函理论(DFT),在B3LYP/6-31G*水平上对135个多氯9,10-菲醌(PCPQ)系列化合物进行全优化和振动分析,得到各分子在298.15K,101.3kPa状态下的热力学参数。设计等键反应,
熔模铸件凝固过程冷却曲线对ProCAST模拟参数的反算求解和优化有重要作用。通过对熔模铸钢件凝固过程冷却曲线的测量方法进行研究并确定铸件内部冷却曲线的测量方法,试验测试
用改进的柠檬酸络合法制备CuO-CexZr1-xO2催化剂,用XRD和TPR研究了催化剂的物理化学性质,无氧条件下研究它对乙醇的催化作用。结果表明,催化剂物相是固溶体CexZr1-xO2,CuO是
考察了聚甲丙烯酸铵酯Ⅰ的流体特性并建立了其动力黏度的测定方法。采用马尔文Kinexus Ultra同轴圆筒式流变仪,测定温度20℃,剪切速率10 s-1。结果表明聚甲丙烯酸铵酯Ⅰ为牛
对基于连续型、时变型及与其他力场联用的三类介电电泳颗粒分离技术进行了综述。分析表明,连续型介电电泳的分离效果较好,但形式较为单一,一般为二元或顺序分离;时变型介电电
Frailty模型和可加故障模型在研究各种风险因素与疾病发生原因的关系中提供了两种重要的方法.在不知哪个模型更适合数据时,涵盖这两个模型的成比例附加故障模型提供了一个备