【摘 要】
：
A kind of aluminum cooler was manufactured by means of vacuum brazing technique, and the cooler was examined by hydraulic pressure test. The result indicates th
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
A kind of aluminum cooler was manufactured by means of vacuum brazing technique, and the cooler was examined by hydraulic pressure test. The result indicates that the test pressure of the cooler can reach 15 MPa. The fracture of the brazing joint belongs to the mixture type. There are secondary cracks, dimples, cleavage plane and grain-boundary features on the failure surface.The cracking process of aluminum cooler is as follows. The cracks are initiated on the interface, then expand under sub-critical state.When the stress on the remained zone reaches the maximum notch tensile strength of the brazing joint or the crack length reaches the critical value that the brazing joint fracture toughness property permits, the cooler will break sharply.
其他文献
By indentation at room temperature followed by annealing at high temperatures, the pinning effect of germanium on dislocations in germanium-doped Czochralski si
The static and dynamic magnetic controlling characteristics of NiMnGa magnetically controlled shape memory alloy (MSMA) were experimentally studied. The results
The hollow sphere fly ash/6061Al composite with about 43% porosity in volume fraction (produced by the addition of hollow sphere fly ash particles) was fabricat
ZnFe2O4-based inert anodes were made to conduct the aluminum electrolysis tests. The corrosion behaviors of the inert anodes were examined and discussed. Experi
A 2D woven graphite fibers reinforced aluminum matrix composite with 50%Grf (volume fraction) was fabricated by the squeeze-casting technology, and its microstr
In Nb-Si based alloys with a two-phase NbSS/ intermetallic Nb5Si3 structure, the Nb5Si3 provides high-temperature strength, while the Nb solid-solution phase, N
The formation mechanism of bulge on the works surface during the extrusion process was analyzed. The bulges size and the reasons for abscission were studied. Th
30%Al2O3p/Al-Cu-2.0Mg composite and Al2O3p/Al-Cu-2.5Mg composite with 0.3 μm-Al2O3 particles were fabricated.Age-hardening behaviors of two composites and the
The technology of length-alterable line-scanning laser sintering was introduced. Based on the research of laser heating property,powder thermal physics paramete
Based on initial discontinuity state (IDS) of material, a preliminary analytical model was presented to evaluate the effect of interaction of pitting corrosion