Effect of Mg addition on the compositions of inclusions were studied. The results show that Mg can minimize the inclusions of steel obviously. Under the present condition, Mg deoxidation products of low-S content experimental steel would be changed in the order of Al2O3→MgAl2O4→Mg–Al–O–S→Mg–O–S. Mg deoxidation products of high-S content experimental steel generate Mg–S(–O)+MnS type inclusions, except for usual oxysulfide. And it is consistent with the results of thermodynamics calculation. Mg is preferred to react with oxide, compared with sulfide. The reaction reaches the equilibrium after 1 min or 5 min. It shows that the number and diameter of inclusions in all experimental steel samples are well under control, helping to improve the properties of steel.
Effect of Mg addition on the compositions of inclusions were studied. The results show that Mg can minimize the inclusions of steel obviously. Under the present condition, Mg deoxidation products of low-S content experimental steel would be changed in the order of Al2O3 → MgAl2O4 → Mg-Al-O-S → Mg-O-S. Mg deoxidation products of high-S content experimental steel generate Mg-S (-O) + MnS type inclusions, except for usual oxysulfide. And it is consistent with the results of the thermodynamics calculation. Mg is preferred to react with oxide, compared with sulfide. The reaction reaches the equilibrium after 1 min or 5 min. It shows that the number and diameter of inclusions in all experimental steel samples are well under control, helping to improve the properties of steel.