Titania is an important catalytic material for photo-catalytic applications, and the sol-gel process is one of the most appropriate technologies to prepare TiO2 thin films. In the present paper, the Ce4+ , Sb3 + -codoped TiO2 films were prepared by sol-gel method, which were heat-treated with an applied electric filed. The phase transformation behavior of Ce4+ , Sb3 + -codoped TiO2 film in the electric field heating-treatment was studied by XRD and AFM. It is found that the crystals were homogeneous and the average crystal size was about 60 nm. Studies of photo-catalytic degradation show that the photo-catalytic activity of Ce4+ , Sb3 +-codoped TiO2 films heated to 500℃in an applied electric field was higher.
Titania is an important catalytic material for photo-catalytic applications, and the sol-gel process is one of the most appropriate technologies to prepare TiO2 thin films. In the present paper, the Ce4 +, Sb3 + -codoped TiO2 films were prepared by sol- gel method, which were heat-treated with an applied electric filed. The phase transformation behavior of Ce4 +, Sb3 + -codoped TiO2 film in the electric field heating-treatment was studied by XRD and AFM. It is found that the crystals were homogeneous and the average crystal size was about 60 nm. Studies of photo-catalytic degradation show that the photo-catalytic activity of Ce4 +, Sb3 + -codoped TiO2 films heated to 500 ° C in an applied electric field was higher.