The Gd substituting effects for La in La0.67Ca0.33MnO3 has been studied. With increasing the substituting amount of Gd, the phase transition temperature of metal-isolator for the samples decreases, the corresponding peak resistivity increases, the Curie temperature decreases monotonically. The substitution of La-Ca-Mn-O with 11% Gd for La improved the magnetoresistance ratio by an order of magnitude. The effects of substituting Gd can be explained in terms of the lattice effects. An irreversible MR behaviour was observed in Gd-substituting compounds. This effect became marked when the substituting amount of Gd was greater than 7%. A maximum irreversible increment of MR ratio as large as 91% was obtained when Gd substituting amount was 11%.
The increasing of the substituting amount of Gd, the phase transition temperature of the metal-isolator for the samples decreases, the corresponding peak resistivity increases, the curie temperature decreases monotonically. The The Gd of substituting effects for La in La0.67Ca0.33MnO3 has been studied. substitution of La-Ca-Mn-O with 11% Gd for La improved the magnetoresistance ratio by an order of magnitude. The effects of substituting Gd can be explained in terms of the lattice effects. An irreversible MR behavior was observed in Gd-substituting A maximum irreversible increment of MR ratio as large as 91% was obtained when Gd substituting amount was 11%.