NiO nanoparticles with average particles size of 30 nm are synthesized using a one-pot metal-organic framework-combustion (MOF-C) technique,for use as an anode material in rechargeable lithium ion batteries (LIBs).The structural and electronic properties
【机 构】
：
Department of Materials Science and Engineering, Chonnam National University, Gwangju 500-757, South
论文部分内容阅读
NiO nanoparticles with average particles size of 30 nm are synthesized using a one-pot metal-organic framework-combustion (MOF-C) technique,for use as an anode material in rechargeable lithium ion batteries (LIBs).The structural and electronic properties of these nanoparticles are studied using various techniques,including powder X-ray diffraction (PXRD),transmission electron microscopy (TEM),scanning electron microscopy (SEM),X-ray photoelectron spectroscopy (XPS),and N2 adsorption/desorption studies.The as-synthesized NiO nanoparticles sustained reversible stable capacities of 748 and 410 mAh/g at applied current densities of 500 and 1000 mA/g,respectively,after 100 cycles.Furthermore,the anode displays a notable rate capability,achieving a stable capacity of ～200 mAh/g at a high current density of 10 A/g.These results indicate that the size of the NiO nanoparticles and their high surface area influence their electrochemical properties.Specifically,this combustion strategy is clearly favorable for improving the cyclability and rate capability of various metal oxides in rechargeable battery electrodes.
其他文献
In the present paper,multi-walled carbon nanotubes (MWCNTs) are successfully assembled on graphite felt (GF) using sucrose pyrolysis method for the first time.The in situ formed pyrolytic carbon is chosen as the binder because it is essentially carbon mat
Selective hydrogenation of biomass-derived 5-hydroxymethylfurfural (HMF) to 2,5-dihydroxymethyl-tetrahydrofuran (DHMTHF) with 96％ selectivity and a complete HMF conversion is obtained over palladium catalyst supported on mesoporous graphitic carbon nitrid
Fluoride mediated nano-sized ZSM-5 (ZSM-5-F) with a high Si/Al ratio of 181 was fabricated using a seed-induction method and evaluated the catalysis of the methanol to propylene (MTP) reaction.High propylene selectivity (45％) was similar to ZSM-5-OH synth
The Li-rich layered oxides show a higher discharge capacity over 250 mAh/g and have been developed into a promising positive material for lithium ion batteries.A rare earth metal oxyfluoride YOF-coated Li[Li0.2Mn0.54Ni0.13Co0.13]O2 composites have been sy
The steam regeneration and SO2 regeneration of tin oxide for warm syngas desulfurization is studied in the temperature range of 400-600 C.In the steam regeneration,reversible removal of H2S achieved.Regenerated H2S concentration increased with the increas
In this work the effects of the contents of nickel (5,7.5,10 wt％) and copper (0,1, 2 wt％) and reaction temperature (650,700,750 ℃) on the catalytic performance of Ni-Cu/Al2O3 catalyst in methane dry reforming were evaluated using Box-Behnken design in ord
A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer (SFMC),sulfonated (poly ether ether ketone) (SPEEK) and 1 or 5 wt％ graphene oxide (GO) was fabricated through a facile so.ution casting approach.The simple,b
The pyrolysis under inert atmosphere has been widely used for the synthesis of metal containing heteroatoms doped carbon materials,versatile catalysts for various reactions.However,it is difficult to prevent metal nanoparticles aggregation during pyrolysi
Reducing the anthropogenic CO2 emissions from fossil resource combustion and human activities has become one of the major challenges we are facing today.Beyond those practical applications for the utilization of CO2,such as the synthesis of salicylic acid
Biobutanol is attracting increasingly interest as a source of renewable energy and biofuels because of its many advantages over bioethanol that include higher energy density,fuel efficiency,and reduced engine damages.Currently,there is a growing interest