【摘 要】
：
The effect of two-stage aging on the microstructures and superplasticity of 01420 Al-Li alloy was investigated by means of OM, TEM analysis and stretching exper
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
The effect of two-stage aging on the microstructures and superplasticity of 01420 Al-Li alloy was investigated by means of OM, TEM analysis and stretching experiment. The results demonstrate that the second phase particles distributed more uniformly with a larger volume fraction can be observed after the two-stage aging (120 ℃, 12 h+300 ℃, 36 h) compared with the single-aging(300 ℃, 48 h). After rolling and recrystallization annealing, fine grains with size of 8-10 μm are obtained, and the superplastic elongation of the specimens reaches 560% at strain rate of 8×10-4 s-1 and 480 ℃. Uniformly distributed fine particles precipitate both on grain boundaries and in grains at lower temperature. When the sheet is aged at high temperature, the particles become coarser with a large volume fraction.
其他文献
V defects in GaN layer grown on Si (111) using metalorganic chemical vapor deposition (MOCVD) were investigated by atomic force microscopy (AFM), plan-view tran
Laser crystal Yb∶KYW was grown by the Kyropoulos method. A grown crystal was identified as β-Yb∶KYW by XRD. By TG-DTA the melting point and transition point
Effects of extrusion deformation and heat treatment on microstructures, mechanical properties and texture of AZ31 Mg alloy were investigated.The results show th
Graphite and Al2O3 short fibers reinforced Mg-Al-Zn alloy hybrid composites were fabricated by perform squeeze-infiltration route. The effects of the volume of
The microstructure and mechanical properties of AZ80 alloy were investigated during thermal processing. The samples of 4 mm in thickness machined from cast ingo
Low energy consumption is one of the main challenges for wireless video transmission on battery limited devices. The energy invested at the lower layers of the
Li3V2(PO4)3 cathode material was prepared by a carbon-thermal reduction (CTR) process. V2O5,LiOH-H2O,NH4H2PO4 and C were used as starting materials to synthesiz
This review provided some recent progress of the research on corrosion mechanisms of magnesium and its alloys and a basis for follow-on research. Galvanic corro
SiCp/1060A1, SiCp/ZL101, SiCp/ZL102 composites with SiCp volume fraction of 55% were fabricated by pressureless infiltration. The microstructure was examined an
The structural, morphological, mechanical and tribological characterization of nanoscaled multilayer TiN/TaN coatings deposited by magnetron sputtering technolo