【摘 要】
：
本文研究了功率密度为(1—1.4)×10~4W/Cm~2激光束对几种常用工具钢T10A、9CrSi、GCr15、CrWMn、W18Cr 4V进行扫描后,表面强化层组织、硬度分布。结果表明激光处理表层硬度比
【机 构】
：
四川工业学院热处理教研室,四川工业学院热处理教研室,四川工业学院物理教研室,四川工业学院物理实验室
论文部分内容阅读
本文研究了功率密度为(1—1.4)×10~4W/Cm~2激光束对几种常用工具钢T10A、9CrSi、GCr15、CrWMn、W18Cr 4V进行扫描后,表面强化层组织、硬度分布。结果表明激光处理表层硬度比普通淬火高,硬度梯度大,硬度沿温度场等效分布。强化层组织一般由2—4层组成,碳化物由表面向内逐渐增多。当扫描速度较小时,表层出现熔变硬化的组织。
In this paper, the microstructure and hardness distribution of the surface strengthened layer after scanning the T10A, 9CrSi, GCr15, CrWMn and W18Cr 4V of several tool steel with the power density of (1-1.4) × 10 ~ 4W / Cm ~ 2 were studied. The results show that the surface hardness of laser treatment is higher than that of ordinary quenching, the hardness gradient is large, and the hardness is equivalently distributed along the temperature field. Fortified layer organization generally consists of 2-4 layers, carbide gradually increased inward from the surface. When the scan speed is small, the surface appears to melt-hardened tissue.
其他文献
笔者对环境介质下用改进WOL型试样测得的δ_(scc)与J_(1scc)之间的关系进行了研究,最后得到了δ_(scc)和J_(1scc)之间定量的关系表达式。
The relationship between δ_ (sc
1.炮六平四马3退42.炮四平六车7退13.炮六平三车3退34.炮三平七象9退75.炮七退二卒1进16.兵二平三卒1进1
1. Cannon Liu Ping Si Ma 3 retreat 42. Gun Siping six car 7 re
我厂一台X50A铣床工作台横向进给丝杠支架(5025025),在右边紧固螺钉的腰形孔处产生断裂,不得不停工检修。因支架系铸坯件,若更换新的,不管外购或自制,都需较长周期,同时又增
改革开放以来,我们对无产阶级专政问题,在理论本源上有新的认识,在文字表述上有一定调整,在内涵解释上有重大变化。
Since the reform and opening up, we have had a new u
我厂是空军后勤的企业化军办工厂,1986年被总后勤部任命为中国人民解放军九五五二工厂,位于武汉东湖之滨,是机械委数显表定点生产厂。技术力量雄厚,设计生产SF系列数显表已
我国可锻铸铁的产量相当长一段时间都排回在年产30万吨的水平上,直到近两年才有了相当大的发展,一跃而为年产45万吨,成为我国第二大铸铁产品(仅次于灰铸铁)。而且已成为我国
一、指甲盖状缺陷的产生图1为我厂采用金属型浇注的气缸盖铸件,其材质是ZQAL9-2,铸件耍求经机加工后,在气压为225kgf/cm2状态下,保压5 min不得泄漏。在设计铸造工艺时,金属
某型导弹弹体大型模胎的材料结构历经硬木、铸铝、环氧塑料及铸铝填敷环氧塑料四次改革。在铸铝模胎上分区段填敷环氧塑料较之浇注法有更多的优越性。填敷法操作方便、节省原
这种工具(图1)能清除钻孔(φ24)后传动轴叉斜面上的毛刺。它由刀杆1及装在刀杆槽内并固定在轴3上的清理刀片4组成。刀杆座内有一弹簧5,能产生清除毛刺所必需的力,并使刀片恒
我厂在研制高精度的球面车床中,上、下回转盘的多环导轨的加工质量直接影响球体的加工精度。多环导轨如图1所示。上、下回转盘各有4条环形导轨,V型槽的夹角为90°,槽的最大