Balance solubility products and enthalpy of formation for NbC0.75 , NbC0.85 , NbC0.88 , NbC and NbN in oriented silicon steels were calculated and compared qualitatively. Meanwhile, the mixing enthalpies of these five Nb compounds were calculated based on Miedema Model. The results show that the solubility products of Nb compounds in ferrite and austenite meet the following relationship, NbC0.75>NbC0.85> NbC0.88>NbC>NbN and NbN has the minimum enthalpy of formation. It indicates that NbN easily precipitate out, but it is more difficult for NbC 0.75 .
Balance solubility products and enthalpy of formation for NbC0.75, NbC0.85, NbC0.88, NbC and NbN in oriented silicon steels were calculated and compared qualitatively. Meanwhile, the mixing enthalpies of these five Nb compounds were calculated based on Miedema Model. The results show that the solubility products of Nb compounds in ferrite and austenite meet the following relationship, NbC0.75> NbC0.85> NbC0.88> NbC> NbN and NbN has the minimum enthalpy of formation. It indicates that NbN easily precipitated , but it is more difficult for NbC 0.75.