A flexible copper clad laminate(FCCL) was fabricated using electroless- and electro-Cu plating processes and the effects of pre-treatment time on the adhesion s
【机 构】
：
School of Advanced Materials Science and Engineering
论文部分内容阅读
A flexible copper clad laminate(FCCL) was fabricated using electroless- and electro-Cu plating processes and the effects of pre-treatment time on the adhesion strength of the FCCL were evaluated based on interfacial morphology. The neutralization and catalyst time were varied in the range of 0-20 min and 0.1-10 min, respectively, and the interfacial condition of the FCCL was characterized by atomic force microscopy(AFM) and X-ray photoelectron spectroscopy(XPS). It is observed that the peel strength increases significantly as the neutralization and catalyst time increase. Peel strength as high as 7.2-7.3 N/cm is obtained as the neutralization and catalyst time increase up to 20 min and 10 min, respectively, which is comparable to the strength achieved by the conventional laminating and sputtering processes. These improvements are probably due to an increase in the surface roughness of polyimide (PI), the activated surface condition, and the adsorption of palladium ions/atoms (Pd) on the PI surface which act as nucleation sites for Cu.
其他文献
Stainless steels such as STS 304, 316 and 630 are frequently used as shaft materials in small fiber reinforced polymer (FRP) fishing boats. If the shaft materia
Methods of optical spectroscopy and X-ray crystallography data were used to examine the effect of architecture of carboxylate anions on structure of the Eu3+ co
Mossbauer spectroscopy has been used to study the morphology of iron oxides formed during the oxidation of superalloys, such as SS-304L (1.4306S), Incoloy-800H,
Friction and wear of the sliding components in an automobile cause an increase in both fuel consumption and emission.Many engine components involved with slidin
The silver-palladium(Ag-Pd) alloy coating as a solid lubricant was investigated for its application to the high temperature stud bolts used in nuclear power pla
The Tb3+-doped Y2O3 nanopowders were synthesized using the modified Pechini method.The average size of nanocrystallites was controlled by different sintering te
The relatively uniform bismuth-copper film was electrodeposited between -15 and -20 mV in the sulfate electrolyte containing 4 mmol/L bismuth ion and 2 mmol/L c
Absorption, excitation and emission spectra as well as decay time measurements at 10, 77, and 300 K were performed for Ga3Gd3Sc2O12 garnet single-crystal doped
Lanthanum hexaboride(LaB6) thin films were deposited on glass substrate by DC magnetron sputtering technology, and the AFM, XRD and scratch tests were used to c
Electron paramagnetic resonance (EPR) and optical absorption studies were carried out at room temperature on copper doped mixed alkali cadmium phosphate (LiNaCd