Effect of tin and antimony on hot ductility of GCr15 bearing steel as well as interaction between lanthanum and tramp dements, were studied by simulator Gleeble-1500 and the fractures for the tested steels were analyzed using SEM and EDS. The results show that with increasing contents of tin and antimony elements, the hot ductility of GCr15 beating steel was decreased. Lanthanum can reduce the harmful effect of tramp elements on the hot ductility of GCr15, which can react with antimony to form compound and segregate at grain boundary in steel. Lanthanum can refine the recrystallized austenite grains after deformation and subsequent martensite structure.