Hypereutectic Al-17.5Si (wt pct) and Al-25Si (wt pct) alloys with various content of rare earth Er were prepared by conventional casting technique. The effect of Er on the microstructure and properties of the hypereutectic Al-Si alloys was investigated using optical microscopy, scanning electron microscopy as well as friction and wear tests. It was found that optimal amount of Er exists in modifying the hypereutectic Al-Si alloys. An appropriate addition of Er improved the anti-wear properties, and reduced the friction coefficient of the hypereutectic Al-Si alloys studied. The primary silicon crystals in the hypereutectic Al-Si alloys were refined with the suitable addition of Er element. The modification mechanism was also discussed in this paper.
Hypereutectic Al-17.5Si (wt pct) and Al-25Si (wt pct) alloys with various content of rare earth Er were prepared by conventional casting technique. The effect of Er on the microstructure and properties of the hypereutectic Al-Si alloys was investigated using optical microscopy, scanning electron microscopy as well as friction and wear tests. It was found that an optimal amount of Er exists in modifying the hypereutectic Al-Si alloys. An appropriate addition of Er improved the anti-wear properties, and reduced the friction coefficient of the hypereutectic Al-Si alloys studied. The primary silicon crystals in the hypereutectic Al-Si alloys were refined with the suitable addition of Er element. The modification mechanism was also discussed in this paper.