论文部分内容阅读
λ-MnO2 was prepared by column method from normal spinel LiMn2 O4 with purity of 99.38%.The influence of LiMn2 O4 grain size and acidity of leaching solution on the lithium leaching process was studied.The results show that the appropriate range of LiMn2O4 grain size was 60- 160 meshes and the concentration of leaching solution HCl was 0.1 mol·L-1.The adsorption capacity Q of λ-MnO2 for lithium increased with the increase of pH and changed markedly at pH 6.0- 10.0. It was 3.80mmol/ g at pH 12.0. The distribution coefficients Kd of Li + and Na + were 3. 406 × 104 and 2. 300 respectively, and the separation coefftcient aLiNa was 1.481×104 at pH 6.5. As a result, λ-MnO2 is a high performance ion-sieve material for lithium ion.