【摘 要】
：
采用金相显微镜、透射电镜对中国低活化马氏体钢(CLAM)在600℃长期时效过程中的显微组织演变规律进行研究。结果表明,随时效时间的延长晶粒发生了一定粗化,晶粒尺寸由时效前
【机 构】
：
贵州大学材料与冶金学院,贵州省材料结构与强度重点实验室,
论文部分内容阅读
采用金相显微镜、透射电镜对中国低活化马氏体钢(CLAM)在600℃长期时效过程中的显微组织演变规律进行研究。结果表明,随时效时间的延长晶粒发生了一定粗化,晶粒尺寸由时效前约8μm增加到10μm(1000 h时效),金相显微组织没有发生明显变化;马氏体板条随保温时间的延长而增大,宽度由时效前的约400 nm增加到约700 nm(1000 h时效)。析出物发生了明显粗化,经过1000 h时效后最大尺寸约为200 nm。
The microstructure evolution of the Chinese low-activation martensitic steel (CLAM) during aging at 600 ℃ was studied by metallographic microscope and transmission electron microscope. The results show that the grain size increases with the aging time, and the grain size increases from about 8μm to 10μm (1000 h aging), and the microstructure does not change obviously. The martensite lath varies with the holding time The width increases from about 400 nm before aging to about 700 nm (1000 h aging). The precipitates have obviously roughened, and the maximum size after aging for 1000 h is about 200 nm.
其他文献
欧洲中世纪出现的骑士是当时时代独特的产物,是当时社会一个新生的社会阶层.谈及骑士制度的影响,可以归纳为两个方面:一是骑士制度对推动当时社会发展起到了举足轻重的作用,
以2-氨基-1-乙酰基葜-3-甲腈和β-二羰基化合物为原料，在1-甲基咪唑-3-丙基磺酸硫酸氢盐的作用下，-锅法合成了薁并[2，1-b]吡啶类衍生物。该反应收率良好、操作简单、条件温和。
半导体一维纳米材料具有独特的光电性质,且相对于零维纳米颗粒,具有良好的电子传输途径,因而在光电化学(PEC)分解水中有着重要的应用前景.TiO2纳米棒和纳米线已被证实具有优
合成了含有取代联苯及烷基硅取代基的二芳基乙炔单体(1a～1d),以TaCl5-n-Bu4Sn作催化剂聚合得到聚合物2a、2b和2d。所得聚合物在常规有机溶剂中具有良好的溶解性。用聚合物2a和
考虑时标上一阶拥有积分边界条件的脉冲动力方程,通过上下解方法结合单调迭代技术得到解存在的充分条件,所得结果包括了周期边值问题、初值问题并且改进和丰富了已有文献的结
为了建立检测硒含量的3,3’-二氨基联苯胺分光光度法,在建立硒测定标准曲线的基础上,进行稳定性试验、加样回收率试验和精密度试验,并通过检测富硒啤酒酵母和壳聚糖硒中的硒
作为一种可设计的新型绿色溶剂,离子液体在样品萃取领域的应用得到越来越多的关注。介绍了离子液体萃取技术在样品前处理领域中的应用研究新进展,包括液-液萃取、液相微萃取
目的 建立尿中2-硫代噻唑烷-4-羧酸(TTCA)测定的反萃取高效液相色谱法.方法 取尿1 ml,分别加入2mol/L盐酸和水各0.5 ml,摇匀,加入4ml乙醚,振荡萃取2min后取出下层水相于具塞
目的 用基质辅助激光解析/电离飞行时间质谱仪(matrix-assisted laser desorption/ionization time-of-flight mass spectrometry,MALDI-TOF MS)比较产KPC型碳青霉烯酶肠杆菌
设G是简单图,图G的一个k-点可区别Ⅳ-全染色(简记为k-VDIVT染色)f是指一个从V(G)∪ E(G)到{1,2,…,k}的映射,满足:(V)uv,uw∈E(G),v≠w,有f(uv)≠f(uw)；(V)u,v∈V(G),u≠v,有C