A new citrate acid-hydrazine sol-gel route for preparation of Co3O4 nanoparticles has been developed. Co3O4 nanoparticles with different particle-sizes and morphology were prepared at different heat-treatment temperatures and the pure cubic nanocrystals of Co3O4 were obtained at 600℃. The synthesis process was monitored by infrared spectroscopy (IR), thermal gravimetric and differential thermal analysis (TG-DTA). The structure and morphology of Co3O4 nanocrystals were characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM) and X-ray-photoelectron spectroscopy (XPS). The infrared absorption bands blueshifted with particle size decreasing, which could be attributed to increasing surface effect. XPS results showed that predominant species at surface layers of Co3O4 nanocrystals are octahedral Co (Ⅲ).