Nanocrystalline zirconia(ZrO) was synthesized using a microwave-hydrothermal process.The effect of pH on the crystallization of the ZrO_2 powders was investigated.The phase and microstructure of ZrO_2 powders were examined using X-ray diffraction(XRD),Raman spectroscopy,and transmission electron microscopy(TEM).Results show that pure m-ZrO_2 can be obtained at low pH(pH<2).Pure t-ZrO_2 is formed at pH = 7 and 14.The size of the ZrO_2 crystals is in the range of 8-26 nm and decreases with increasing pH.The formation of m-ZrO_2 results from the precipitation of ZrO_2 from solution.The t-ZrO_2 is formed through the in-situ structural rearrangement of amorphous Zr(OH)_xO_y.The stabilization of t-ZrO_2 is attributed to the small crystal size and the adsorption of hydroxy ions on the surfaces of the crystals.
The effect of pH on the crystallization of the ZrO 2 powders was investigated. Phase and microstructure of ZrO_2 powders were examined using X-ray diffraction (XRD), Raman spectroscopy, and Transmission electron microscopy (TEM). Results show that pure m-ZrO 2 can be obtained at low pH (pH <2). Pure t-ZrO 2 is formed at pH = 7 and 14. The size of the ZrO 2 crystals is in the range of 8-26 nm and decreases with increasing pH. The formation of m-ZrO 2 results from the precipitation of ZrO 2 from solution. T-ZrO 2 is formed through the in-situ structural rearrangement of amorphous Zr (OH) _xO_y.The stabilization of t -ZrO_2 is attributed to the small crystal size and the adsorption of hydroxy ions on the surfaces of the crystals.