【摘 要】
：
Phase composition and microstructures of grain boundary of oversintered yttrium aluminum garnet (Y3Al5O12, YAG) ceramics by vacuum sintering at 1 850 ℃ were in
【机 构】
：
Center for Composite Materials
论文部分内容阅读
Phase composition and microstructures of grain boundary of oversintered yttrium aluminum garnet (Y3Al5O12, YAG) ceramics by vacuum sintering at 1 850 ℃ were investigated. For synthesizing YAG, grain boundary is a key factor for YAG ceramics. The morphology of grain boundary was observed by SEM, TEM and its composition was analyzed by EDS. It is identified that the grain boundary is composed of α-Al2O3 and yttrium aluminum perovskite (YAP, YAlO3) eutectics. At the edge of YAG crystal grain, YAG phase is decomposed into perovskite YAP and α-Al2O3 during high temperature sintering. Due to refractive indexes of YAP and α-Al2O3 phases in wide grain boundary are different from those of YAG, the transmittance of oversintered YAG ceramics is lower than that of YAG ceramics sintered at 1 750 ℃.
其他文献
The doping effect of rare earth elements (Tb and Sm) on the electronic structure of (110) martensitic twin boundary in Ni2MnGa alloys was investigated by using
The fabrication of one kind of large core area Nd3+ doped silicate glass photonic crystal fiber, and demonstration of the fibers waveguidence properties were re
M-type hexaferrites BaLaxFe12-xO19 powders were synthesized by sol-gel method in the presence of SiO2 nanoparticles. The X-ray diffraction patterns of BaLaxFe12
The microstructures of mechanical alloyed(MA) Ti-12%Mg alloy powders were examined using a high resolution TEM (HRTEM). The effect of MA atmospheres such as arg
The ceramic coatings containing zirconium dioxide were grown in-situ on LY12 aluminium alloy by micro-arc oxidation in mixed zirconate and phosphate solution. T
Li-storage intermetallic compound FeSb2 was prepared by solvothermal method and was studied as a promising anode material for secondary lithium-ion batteries. T
The effect of interstitial hydrogen on the cohesion of the Al ∑=11(113) grain boundary (GB) is investigated based on the thermodynamic model of Rice-Wang using
AlGaAs/GaAs multi-quantum well (MQW) was prepared by molecular beam epitaxy(MBE) with growth-interrupted heterointerface (GIH) method and continuous growth (CG)
The effect of vacuum heat treatment on the microstructure and microhardness of cold-sprayed Cu-4%Cr-2%Nb alloy coating was investigated. The heat treatment was
Mortar prisms were made with three different cementitious materials (with or without mineral admixture) plus 30% mass of limestone filler. After 28 days of curi