The relationship between electromagnetic frequency and microstructures of continuous casting aluminum alloys was studied. 7075 aluminum alloy ingot of 100 mm in diameter was produced by electromagnetic continuous casting process, the microstructures of as-cast ingot was examined by scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS). The results showed that electromagnetic frequency greatly influenced segregation and microstructures of as-cast ingot, and product quality can be guaranteed by the application of a proper frequency. Electromagnetic frequency plays a significant role in solute redistribution; low frequency is more efficient for promoting solution of alloying elements.
The relationship between electromagnetic frequency and microstructures of continuous casting aluminum alloys was studied. 7075 aluminum alloy ingot of 100 mm in diameter was produced by electromagnetic continuous casting process, the microstructures of as-cast ingot was examined by scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS). The results showed that electromagnetic frequency greatly influenced segregation and microstructures of as-cast ingot, and product quality can be guaranteed by the application of a proper frequency. Electromagnetic frequency plays a significant role in solute redistribution; low frequency is more efficient for promoting solution of alloying elements.