【摘 要】
：
Graded porous scaffold can be applied to study the interactions between cells and scaffold with different pore sizes.Polydimethylsiloxane(PDMS)scaffold with an axial pore size grade was successfully manufactured via vacuum-assisted resin transfer moulding
【机 构】
：
School of Materials Science and Engineering,Fujian University of Technology,Fuzhou 350118,China;Fuji
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Graded porous scaffold can be applied to study the interactions between cells and scaffold with different pore sizes.Polydimethylsiloxane(PDMS)scaffold with an axial pore size grade was successfully manufactured via vacuum-assisted resin transfer moulding(VARTM)and particle leaching technologies.The properties of graded PDMS scaffolds,including porosity,water absorption,interconnectivity,compression modulus,as well as compression strength were investigated.The results showed that the smaller the size of the NaCl particles is,the higher the porosity and water absorption of graded PDMS scaffolds would be.The graded PDMS scaffold fabricated had a compressive modulus and a compressive strength of 19.69±1.42 kPa and 4.76±0.22 kPa,respectively.Moreover,the graded chitosan(CS)-coated PDMS scaffolds were prepared by using dip-coating technique under low vacuum and their hydrophilicity was examined.It is found that the water contact angle(WCA)will decrease with an increase in the CS solution concentration and the coating time,which indicates that CS-coated PDMS scaffolds exhibit noticeable hydrophilicity compared with graded PDMS scaffold.
其他文献
Backscattered electron images (BSE) obtained by scanning electron microscope was used to quantitatively characterize the microstructure of interfacial transition zone (ITZ) in concrete. Influences of aggregate size (5, 10, 20, and 30 mm), water to cement
Vanadium trioxide (V2O3) was directly prepared by NaVO3 electrolysis in NaCl molten salts. Electrolysis products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The existing state
Yield stress development of cement paste is potentially governed by percolation of 3-dimensional links formed by hydration products on the surface of the particles. It rises steadily at a gradual rate before a sudden increase in rate of growth. In this st
Mg0.2Zn0.8O (MZO)/La0.67Ca0.33MnO (LCMO) heterostructure was deposited on p+-Si substrates by sol-gel spin coating technique.The Ag/MZO/LCMO/p+-Si devices exhibit a bipolar,reversible,and remarkable current-voltage characteristic at room temperature.An ob
Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity (Erd values) were mon
For refining grain and obtaining excellent properties,the experiments of asymmetric and symmetric monotonic hot roiling were carried out to investigate the role of shear strain on the microstruetures and mechanical properties of V-microalloyed steel.The s
The microstructure,tensilc property and wear resistance of 7075 aluminum matrix composite reinforced with TiC particles prepared by in-situ reaction casting were investigated.The effect of TiC reinforcement on wear behavior was analyzed.The wear mechanism