【摘 要】
：
AlCrN coating was prepared on the surface of TiC-based cermet cutting tool with cathodic arc ion plat-ing,and the surface-interface morphologies,compositions of
【机 构】
：
College of Mechanical Engineering,Changzhou University,Changzhou 213164,China;School of Petrochemica
论文部分内容阅读
AlCrN coating was prepared on the surface of TiC-based cermet cutting tool with cathodic arc ion plat-ing,and the surface-interface morphologies,compositions of chemical elements,and phases were analyzed by scan-ning electron microscope(SEM),energy dispersive spec-trometer(EDS),and X-ray diffraction(XRD),respectively.Bonding strength of the coating-substrate interface was measured with scratching test,and the wear mechanism and friction coefficient of TiC-based cermet cutting tool and AlCrN coating were investigated with friction and wear testing machine.The results show that the interface binding of AlCrN coating is metallurgical mode,and its binding strength is 83 N.The average friction coefficient of TiC-based cermet cutting tool under the load of 6 N is 0.8409,while that under the load of 8 N decreases by about 11％,and the wear mechanism of TiC cermet cutting tool is fatigue wear,abrasive wear,and oxidation wear.The average friction coefficient of AlCrN coating is 0.6363 under the load of 6 N,and the change is relatively stable,decreasing by about 25％than that of TiC-based cermet cutting tool;when the load increases to 8 N,the average friction coefficient of AlCrN coating decreases by 9％.The wear mechanism of AlCrN coating is abrasive wear and oxidation wear,showing lower friction coefficient and good wear resistance.
其他文献
异径四通是过程工艺和物料运输中常用的管件,采用弹塑性有限元方法对异径四通塑性极限内压进行研究,分析异径四通的破坏过程及失效特征,明确了主管径厚比、支主管径比、过渡圆角与外径比、支主管壁厚比等尺寸参量对异径四通极限载荷的影响并得出相应的影响曲线,建立了常用尺寸范围内异径四通管件塑性极限内压工程估算式。研究结果可为四通管件优化设计和含缺陷结构的完整性评定提供参考。
Corrugated cold roll bonding(CCRB)produces metal composite plate with improved mechanical proper-ties compared with conventional methods,but the interfa-cial me
分别采用316LMn,385,317L,308L和316L的焊条和氩弧焊丝焊接SUS304L,重点研究了焊缝金属在经过570℃×1 h热处理后-196℃冲击吸收能量及焊接工艺性能。385和316LMn全奥氏体熔敷金属低温韧性优异且稳定性好,308L,317L和316L的焊条和焊丝,通过优化平衡Cr,Ni当量控制铁素体数小于3,焊缝金属-196℃冲击值稳定在50 J以上。熔敷金属为全奥氏体的焊材焊接时,需要控制线能量,防止出现热裂纹,当熔敷金属Mn含量较高时,可以有效减少热裂纹的产生。SUS304L设备焊材
断路器是用来接通或断开电路,尤其是在电力系统发生短路故障时,断路器迅速动作将故障点切除,断路器工作性能好坏除了与本身的电气、机械、绝缘等性能有关,还与其控制、保护及二次回路接线是否完善合理有很大关系。某变电站110 kV断路器跳闸出口压板接地,造成断路器操作箱TBJ电流保持继电器励磁动作,导致运行中的断路器跳闸,本文对其动作原因进行分析,并提出防范断路器操作箱TBJ误动作风险改进措施和建议。
目前,在断路器传统本体三相不一致保护回路中,当断路器处于合闸状态时,三相不一致保护出口中间继电器故障或人员误碰会使回路接通,导致断路器误动作。针对这类问题,本文通过传统断路器本体三相不一致的回路分析,提出了四种可以改进的方案,详细分析了每一种方案的优缺点,列举了方案选择错误的实例,总结出现场应正确选择相应的方案进行优化改进,才能有效防止人为误碰、外力作用或三相不一致的继电器故障等原因引起的本体三相不一致保护误动,提高电网运行的可靠性。
低温低应力工况是压力容器用碳钢低合金钢在低温领域应用的重要保障,我国压力容器规范低应力工况仅为欧美规范的特例,其工程应用受限。分析了ASMEⅧ与EN 13445中低应力工况温度调整曲线理论背景,研究了板厚与强度对温度调整值的影响规律。在此基础上,建立基于主曲线法的低应力工况温度调整准则,发现压力容器规范缺乏科学合理的最低设计温度确定方法是限制我国压力容器用钢在低温下服役的根本原因。
采用模块化施工方法,对甲醇制烯烃(MTO)反应器进行分段预制、拆除及安装。从设计选材、制造组焊工艺、安装顺序等环节进行了优化,提高了反应器预制安装质量,降低了施工过程中的安全风险、节约了施工过程中人工及机械费用的支出,解决了已经建造完毕的厂区内无法运输直径和长度较大设备、MTO反应器整体更换需对原装置框架进行大量拆除以及检修改造项目工期紧而不允许进行长周期作业的问题。为类似新建或改造装置模块化施工提供了参考。
电力行业,向来是一个中心化监管和调配市场供需的行业,区块链作为一个带着“去中心化”光环的技术,能够为电力行业带来怎么样的变革?当前电力行业正处在快速变革期,由于可再生能源的出现以及分布式能源的研究,能源储存方式、能源利用效率以及能源数字化都在加速变迁,区块链的诞生为计量这些不确定性提供了新的路径。区块链技术作为继大数据、云计算和人工智能之后的一项新技术,中南财经政法大学数字经济研究院执行院长、教授、南方电网专家委员会委员盘和林建议,在电网企业中,可以把区块链放在和大数据、云计算和人工智能同等重要的位置。
介绍了采用锻-轧结合工艺生产12Cr2Mo1VR钢板的技术要求、工艺控制要点及实物质量。通过对冶炼、锻造、轧制及热处理工艺进行优化并精确控制,钢板的成分、金相组织、超声检测质量等级、常规力学性能及步冷脆化试验结果满足技术要求,部分实物质量已与进口阿赛洛钢板水平相当。
云南省独特的地理地貌以及多变的气候因素,造就了云南省森林火灾易发且发展迅速的特点。针对云南电网范围内架空输电线路以及电网设备可能遭受的森林火灾问题,开展林火蔓延研究,重点突破运用Rothermel模型和惠更斯原理相结合的方法对林火蔓延进行实时模拟,在此基础上,运用ArcGIS的图形处理和空间分析能力,对蔓延过程进行图形化显示,为电网开展一次设备山火风险防控工作提供有力支撑。