The aging properties of Cu-0.35Cr-0.038Zr-0.055Ce alloy are studied. The results show that can obtain higher electrical conductivity and microhardness after sol
【机 构】
：
School of Material Science & Engineering,School of Materials and Chemical
【基金项目】
：
国家高技术研究发展计划(863计划)
论文部分内容阅读
The aging properties of Cu-0.35Cr-0.038Zr-0.055Ce alloy are studied. The results show that can obtain higher electrical conductivity and microhardness after solutioned at 920℃for lh, and aged at 500℃. The process of precipitation of the secondary phase can be accelerated with cold deformation before aging, so properties of the alloy are improved.Upon aging at 500℃ for 30 minutes after 60% cold deformation, the values of electrical conductivity and microhardness are69.0%IACS and 152HV respectively, but they are only 66.2%IACS and 136HV upon directly aging after solution. With the addition of a trace of rare earth element Ce, the value of microhardness of Cu-0.35Cr-0.038Zr alloy increases 18～25HV,while the value of electrical conductivity drops a little.
其他文献
The surface of Ti-50.8Ni at% shape memory alloy was melted by an Nd-YAG laser. The Ti/Ni and Ti4+/Ti atomic concentration ratios at the surface were changed sig
Laser cladding is performed to improve the surface properties of metallic machine components. Extensive work is being conducted to investigate the relationships
Laser surface remelting of medium Ni-Cr infinite chilling cast iron was performed with a continuous wave CO2 laser beam with the power of 7 KW under the argon s
Ordering and atom clustering in aging binary Al-Li alloy has been investigated by computer simulation through calculating the long range order (lro.) parameter
This work reports research concerning the microstructure and sliding wear behaviour of cermet coatings deposited by high velocity oxy-fuel (HVOF) spraying. Two
This paper deals with the kinetics of compound layer growth of steel En40B plasmas nitrided at 520℃ for different time and establishes the corresponding mathem
Degradation phenomena like wear and corrosion, may have their effects accelerated as components operate at high temperature. The aim of this work is to make an
Low cycle fatigue behaviour of a steel 55NiCrMoV7 under four tempered conditions is reported. One special type of total strain controlled isothermal cyclic defo
The development of materials technologies, including surface engineering is one of the main trends in the knowledge-based economy. The direct advantages of the
In order to well design tribosystems of dental CAD-CAM restorations, an understanding of the tribological mechanisms of dental machinable porcelain are essentia