【摘 要】
：
用固相反应法制备了Na_5Y_(1-x)Cr_xSi_4O_(12)导电陶瓷。用x-射线衍射,红外光谱,透射电镜研究了晶相和显微结构。用导纳电桥测定了样品室温至350℃的电导率,得出最佳组分X=0
【机 构】
：
武汉工业大学硅工系,武汉工业大学硅工系,武汉工业大学硅工系
论文部分内容阅读
用固相反应法制备了Na_5Y_(1-x)Cr_xSi_4O_(12)导电陶瓷。用x-射线衍射,红外光谱,透射电镜研究了晶相和显微结构。用导纳电桥测定了样品室温至350℃的电导率,得出最佳组分X=0.05,该样品电导率σ300℃=1.80×10~(-1)(Ω·cm)~(-1)。证明简单跳跃模型在高温下是合理的。
Na_5Y_ (1-x) Cr_xSi_4O_ (12) conductive ceramics were prepared by solid-state reaction. The crystal phase and microstructure were investigated by x-ray diffraction, infrared spectroscopy and transmission electron microscopy. The conductivity of the sample was measured at room temperature to 350 ℃ with an admittance bridge, and the best composition X = 0.05 was obtained. The conductivity of the sample was σ300 ℃ = 1.80 × 10 -1 (Ω · cm) -1 ). It is proved that the simple jump model is reasonable at high temperature.
其他文献
用扫描电镜、透射电镜和 X 射线衍射研究了 Si_3N_4-TiC-Co 系复合材料的相组成、显微结构和力学性能。发现 TiC 以 TiC 和 TiN 形式存在,Co 以 CoSi 形式存在。加入 TiC 和
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
本文论述了我国保险合同解释存在的问题以及我国保险合同解释原则的适用性问题。
This article discusses the problems existing in the explanation of insurance contrac
本文对Fe-Mo-MoS_2系材料进行了研究,并考察了该系材料中Fe/Mo比对性能的影响。结果表明,该系材料在摩擦状态下具有较好的减摩性能。在实际PV值高达200～300kg.m/cm~2。S时,摩
“不是为了回报,所以关怀;不是为了明天,所以期待……只是为了你一点进步,只是为了你一个笑容,爱就存在!”——题记站在讲台的第一天,面对45名活泼可爱的孩子,我默默地承诺:
金口材料晶界研究的班状和发展··················“···“···························……‘’·····,····……
日本东京大学工学院开发了一种蒸发速度提高一千倍的超导电陶瓷膜制造工艺,该工艺把原来用于制取合金微粒子的高频热等离子法转用到制造超导电陶瓷膜上,每分钟的堆积速度高
信托制度移植到大陆法系后,信托财产所有权归属问题一直被学界所关注。本文探讨两大法系不同背景下的所有权理念、概念、特征和制度规范的差异,从概念层面的解构到理论层面的
随着科学技术的飞跃发展,有必要对长度基本单位——米所下的定义,要求得更加严密一些。现在是处于微米技术时代,例如大规模集成电路和粉体超微粒子等微米加工技术在不断发展